The present invention relates to the field of plastic products, in particular to a plastic surface metallization method, including: cleaning of plastic products, removal of impurities on the surface of a plastic product placement; roughening treatment device for roughening treatment; the roughening treatment after the plastic products in a vacuum environment, by wire the evaporation and condensation, formation of metal thin film on the surface of plastic products, the plastic products placed directly in the vacuum environment coarsening after treatment in treatment, compared with the existing technology in copper plating plating, can be avoided and the residual heavy metal ions to reduce pollution, conserve resources.
【技术实现步骤摘要】
本专利技术涉及塑料制品领域，尤其涉及。
技术介绍
塑料为合成的高分子化合物，又可称为高分子或巨分子，也是一般所俗称的塑料或树脂，可以自由改变形体样式，是利用单体原料以合成或缩合反应聚合而成的材料，由合成树脂、填料、增塑剂、稳定剂、润滑剂和色料等添加剂组成的，现有的塑料表面金属化技术采用在铜镀液中进行施镀，存在重金属离子的使用及残余等问题，对环境造成了较为严重的污染。
技术实现思路
本专利技术的目的在于提出，能够避免重金属离子的使用及残余，降低污染，节约资源。为达此目的，本专利技术采用以下技术方案:—种塑料制品表面金属化方法,包括:步骤a、对塑料制品进行清洗，去除其表面带有的杂质；步骤b、将塑料制 品置入粗化处理装置中进行粗化处理；步骤C、将粗化处理后的塑料制品置于真空环境中，通过金属细丝的蒸发和凝结，在塑料制品表面形成金属薄膜。其中，粗化处理装置包括:电动砂轮、定位装置及自动移动装置。其中，金属细丝为铝、锡、铜或镍中的一种或几种。其中，金属薄膜的厚度为0.2-0.4毫米。本专利技术的有益效果为:，包括:对塑料制品进行清洗，去除其表面带有的杂质；将塑料制品置入粗化处理装置中进行粗化处理；将粗化处理后的塑料制品置于真空环境中，通过金属细丝的蒸发和凝结，在塑料制品表面形成金属薄膜，本专利技术将粗化处理后的塑料制品直接置于真空环境中进行处理，与现有技术置入铜镀液中施镀相比，能够避免重金属离子的使用及残余，降低污染，节约资源。【附图说明】图1是本专利技术【具体实施方式】提供的流程图。【具体实施方式】下面结合图1并通过【具体实施方式】来进一步说明本专利技术的...
【技术保护点】
一种塑料制品表面金属化方法，其特征在于，包括：步骤a、对塑料制品进行清洗，去除其表面带有的杂质；步骤b、将塑料制品置入粗化处理装置中进行粗化处理；步骤c、将粗化处理后的塑料制品置于真空环境中，通过金属细丝的蒸发和凝结，在塑料制品表面形成金属薄膜。
【技术特征摘要】
1.一种塑料制品表面金属化方法，其特征在于，包括: 步骤a、对塑料制品进行清洗，去除其表面带有的杂质； 步骤b、将塑料制品置入粗化处理装置中进行粗化处理； 步骤C、将粗化处理后的塑料制品置于真空环境中，通过金属细丝的蒸发和凝结，在塑料制品表面形成金属薄膜。2.根据权利要求1所述的一种塑料制...
【专利技术属性】
技术研发人员：吴镇宇，
申请(专利权)人：昆山市华浦塑业有限公司，
类型：发明