The purpose of this invention is to provide a low cost of austenitic stainless steel excellent in corrosion resistance, which is based on the 18-8 austenitic stainless steel, austenitic stainless steel with excellent corrosion resistance and low cost advantages, its strength, ductility and corrosion resistance to dilute sulfuric acid, phosphoric acid and other reducing medium at or near 316 and 316L austenite the level of difficulty in manufacturing stainless steel, with 316 and 316L austenitic stainless steel, can be used for high requirements on the corrosion resistance of chemical, energy and other fields, but its production cost is 316 and 316L austenitic stainless steel is greatly reduced.
【技术实现步骤摘要】
【专利摘要】本专利技术的目的是提供一种耐腐蚀性能优良的低成本奥氏体不锈钢，其是基于18-8奥氏体不锈钢的基础上，具有优良耐蚀性和低成本优势的奥氏体不锈钢，其强度、塑韧性及耐稀硫酸、磷酸等还原性介质腐蚀性能达到或接近316和316L奥氏体不锈钢的水平，生产制造难度与316和316L奥氏体不锈钢相当，可用于对耐腐蚀性能要求较高的化工、能源等领域，但其成产成本较之316和316L奥氏体不锈钢却大大降低。【专利说明】一种耐腐蚀性能优良的低成本奥氏体不锈钢
本专利技术涉及一种奥氏体不锈钢，尤其涉及一种耐腐蚀性能优良、成本低廉的奥氏体不锈钢。
技术介绍
18-8系列奥氏体不锈钢(如304)中较高含量的铬元素保证了其具有优良的耐腐蚀性能，尤其对氧化性酸(如硝酸)具有很强的耐腐蚀性能，对碱溶液及大部分有机酸和无机酸也有一定的耐腐蚀性能力，该类钢种中大于8%的镍含量保证了其具有优良的室温塑性和成型性能，其固溶态组织为奥氏体加少量的铁素体组织，微量的铁素体组织保证了其优良的焊接性能，亚稳组织保证了其在冷加工变形中可以通过马氏体形变而强化，由于具有以上优异的各方面性能，因此304是奥氏体不锈钢中生产量和使用量最大的钢种之一，主要用于化工、能源、炼油等领域。然而在一些对耐点蚀性和耐均匀腐蚀性能要求比较高的领域，其耐腐蚀性能仍然不能满足要求。316是在18-8型Cr-Ni奥氏体不锈钢的基础上，添加了 2~3%的Mo元素和2~4%的镍元素而发展起来的，由于Mo在奥氏体不锈钢中的主要作用是提高钢的耐还原性介质的腐蚀性能、耐点蚀性能和耐缝隙腐蚀等性能，因此Mo的添加使18-8型奥...
【技术保护点】
一种耐腐蚀性能优良的低成本奥氏体不锈钢，其化学元素质量百分配比为：C≤0.04%；Cr?16.00%～19.00%；Ni?8.00%～10.00%；Mo?0.50%～1.50%；Cu?2.10%～4.50%；N?0.02%～0.08%；Mn≤0.80%；Si?1.30%～2.50%；P≤0.04%；S≤0.005%；B?0.0010%～0.0040%；余量为Fe和其他不可避免的杂质；且Si/Mn为2.5～4。
【技术特征摘要】