分层三维石墨烯/γ-三氧化二铁磁性纳米片阵列及其合成方法技术

本发明专利技术公开了一种分层三维石墨烯/γ-三氧化二铁磁性纳米片阵列及其合成方法，用本发明专利技术的石墨烯/γ-三氧化二铁纳米复合材料制备20wt％石墨烯/γ-三氧化二铁-石蜡复合薄膜材料，通过电磁参数的测定和不同薄膜厚度的电磁波反射率的计算结果可知：利用石墨烯/γ-三氧化二铁纳米复合材料制备的薄膜，在其厚度为2-5毫米时，吸收强度均达到了-15dB以下，其吸收频率宽度很大。制备薄膜所需的材料比例很小，薄膜材料中石墨烯/γ-三氧化二铁材料含量低于20wt％，所以用料更少，制作的薄膜材料材质更轻，更有利于工业化生产，应用也更广泛。

The three-dimensional layered graphene / gamma Fe2O3 nano magnetic film array and its synthesis method

The invention discloses a three-dimensional layered graphene / gamma Fe2O3 nano magnetic film array and its synthesis method, with the invention of graphene / gamma ferric oxide nano composite preparation of 20wt% graphene / gamma ferric oxide paraffin composite film materials, the calculation results of electromagnetic wave reflectivity measured by electromagnetic parameters and different film thickness the results show that: the use of graphene / gamma ferric oxide nano composite films prepared in the thickness of 2-5 mm, the absorption intensity reached -15dB, the absorption frequency width. The preparation of thin film materials required for a very small proportion of the film material, graphene / gamma ferric oxide material content is less than 20wt%, so use less material, film made of lighter, more conducive to industrial production, also applied more widely.

【技术实现步骤摘要】

【技术保护点】
一种分层三维石墨烯/γ?三氧化二铁磁性纳米片阵列的合成方法，其特征在于包括以下步骤：(1)G/β?FeOOH模板的制备：向石墨烯水溶液中加入Fe(NO3)3·9H2O，石墨烯和Fe(NO3)3·9H2O质量比为1∶100，并将获得的混合溶液在50℃下搅拌两个小时；然后将获得的沉淀物离心分离出来，用蒸馏水和乙醇清洗后，在真空环境下干燥；(2)G/β?FeOOH纳米片阵列的合成：将FeCl3·6H2O溶于水，加入硝酸钠；溶解后加入G/β?FeOOH模板，超声至分散均匀；5克FeCl3·6H2O对应模板的用量为0.15克；置于高压釜内60℃，水热反应12小时；沉淀用蒸馏水和乙醇清洗几次，在真空的环境下干燥；(3)石墨烯/γ?三氧化二铁纳米复合材料的制备：将已干燥的G/β?FeOOH纳米片陈列在空气下加热到300℃，退火处理2个小时，即得所需产品。

【技术特征摘要】

【专利技术属性】
技术研发人员：任玉兰，
申请(专利权)人：牡丹江师范学院，
类型：发明
国别省市：