一种防冻混凝土制造技术

本发明专利技术属于建筑材料技术领域，特别涉及一种防冻混凝土。针对现有技术的不足，本发明专利技术提供一种安全性高，适应高寒地区冬季的防冻混凝土。本发明专利技术的技术方案是一种防冻混凝土，成分包括水泥、尿素、碳酸盐、硅粉、珍珠岩、氯化钙、砂和外加剂，按配比为：水泥29~32，尿素2~4，碳酸盐2~8，硅粉33~39，珍珠岩22~32，氯化钙2~6，砂23~29，外加剂1~1.5。与现有技术相比，本发明专利技术所具有的有益效果为：本发明专利技术综上所述，该混凝土由于加入了尿素、碳酸盐、硅粉、珍珠岩、氯化钙等防冻材料，使得该混凝土具有优秀的防冻能力，适合高寒地区冬季的施工作业。

Antifreezing Concrete

The invention belongs to the technical field of building materials, in particular to an antifreezing concrete. In view of the deficiency of the prior art, the invention provides an antifreezing concrete with high safety and suitable for winter in the alpine region. The technical scheme of the invention is a kind of antifreeze concrete components, including cement, urea, carbonate, calcium chloride, silica powder, perlite, sand and cement, according to the ratio is: cement 29~32, urea 2~4, carbonate 2~8, 33~39 powder, perlite 22~32, calcium chloride 2~6, 23~29 sand, additive 1~1.5. Compared with the prior art, the invention has the beneficial effect of the invention is: To sum up, the concrete due to the addition of urea, carbonate, silica powder, perlite, calcium chloride and other antifreeze material, makes the concrete with antifreezing ability, suitable for winter construction in cold area.

【技术实现步骤摘要】
一种防冻混凝土
本专利技术属于建筑材料
，特别涉及一种防冻混凝土。
技术介绍
高寒地区冬季的一般为了保证建筑材料的品质和施工质量，一般冬季建筑施工很难进行，这样不仅耽误工期，而且就算强行施工也很难保证建筑的质量，造成安全隐患。
技术实现思路
针对现有技术的不足，本专利技术提供一种安全性高，适应高寒地区冬季的防冻混凝土。本专利技术的技术方案是一种防冻混凝土，成分包括水泥、尿素、碳酸盐、硅粉、珍珠岩、氯化钙、砂和外加剂，按配比为:水泥29~32，尿素2~4，碳酸盐2~8，硅粉33~39，珍珠岩22~32，氯化钙2飞，砂23~29，外加剂f 1.5。与现有技术相比，本专利技术所具有的有益效果为:本专利技术综上所述，该混凝土由于加入了尿素、碳酸盐、硅粉、珍珠岩、氯化钙等防冻材料，使得该混凝土具有优秀的防冻能力，适合高寒地区冬季的施工作业。【具体实施方式】本专利技术详细内容结合实施例加以说明。一种防冻混凝土，成分包括水泥、尿素、碳酸盐、硅粉、珍珠岩、氯化钙、砂和外加剂，按配比为:水泥29~32，尿素2~4，碳酸盐2~8，硅粉33~39，珍珠岩22~32，氯化钙2飞，砂23~29，外加剂I~1.5。

【技术保护点】
一种防冻混凝土，其特征在于：成分包括水泥、尿素、碳酸盐、硅粉、珍珠岩、氯化钙、砂和外加剂，按配比为：水泥29~32，尿素2~4，碳酸盐2~8，硅粉33~39，珍珠岩22~32，氯化钙2~6，砂23~29，外加剂1~1.5。

【技术特征摘要】
1.一种防冻混凝土，其特征在于:成分包括水泥、尿素、碳酸盐、硅粉、珍珠岩、氯化钙、 砂和外加剂，按配比为:水泥29...

【专利技术属性】
技术研发人员：杨博葳，
申请(专利权)人：杨博葳，
类型：发明
国别省市：