The invention discloses a process for producing a moisture-proof wallpaper, the production process comprises the steps: selection of raw materials, respectively, silicon rubber binder; step two: silicone rubber and adhesive according to the weight ratio of 8:2 mixture; step three: the mixture is put into grinding particle size in a blender. The particle diameter is 0.5mm-1mm; step four: the mixture of particle size on the extrusion in the mold, made of semi-finished products, the pressure of 280MPa-330MPa, temperature of 120 DEG -180 DEG C; cooling; step five: step six: the semi-finished products are placed after the cold embossing embossing machine in seven steps; the semi-finished products after embossing a surface coated with color, made of finished products; step eight: the finished airing, winding. The invention has the advantages of simple process, moisture resistance and mildew resistance.
【技术实现步骤摘要】
本专利技术涉及一种墙纸的工艺，尤其涉及一种防潮墙纸的生产工艺。
技术介绍
目前，随着时代的发展，追求生活质量和品位的人越来越多，如何将家装扮的更加温馨和时尚，是越来越多的人的需求，而墙纸正好能满足大众这样的一种要求，让个性十足无处不在。而人们对墙纸的性能也要求的越来越多，比如是否具有印花或者是否可以防潮、防霉效果，而现有技术中的纸制品还不能满足上述要求。
技术实现思路
本专利技术所要解决的技术问题是提供一种工艺简单、防潮、防霉的墙纸的生产工艺。为解决上述技术问题，本专利技术所采用的技术方案是:一种防潮墙纸的生产工艺，该生产工艺依次包括: 步骤一:选取原材料，分别为硅橡胶、粘结剂； 步骤二:将硅橡胶与粘结剂按照重量比为8:2的比例混合； 步骤三:将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.5mm-1mm ；步骤四:将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为280MPa-330MPa，温度为 120°C -180°C ； 步骤五:冷却； 步骤六:将所述冷却后的半成品放在压花机中压花； 步骤七:将压花后的半成品表面涂上色彩，制成成品； 步骤八:将所述成品晾干，收卷。所述颗粒直径为0.8mm。所述压力为300MPa。所述温度为150°C。与现有技术相比，本专利技术的有益效果为: 由于本专利技术防潮墙纸的生产工艺采用了合理的原料及科学的工艺步骤及条件，所以能够制作出防潮、防霉的墙纸，适用于厨房和卫生间，且制作工序少、易操作，因此本专利技术工艺简单、防潮、防霉。具体实施例方式以下结合具体实施方式详细说明本专利技术 一种防潮墙...
【技术保护点】
一种防潮墙纸的生产工艺，其特征在于：该生产工艺依次包括：步骤一：选取原材料，分别为硅橡胶、粘结剂；步骤二：将硅橡胶与粘结剂按照重量比为8：2的比例混合；步骤三:?将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.5mm?1mm；步骤四：将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为280MPa?330MPa，温度为120℃?180℃；步骤五：冷却；步骤六：将所述冷却后的半成品放在压花机中压花；步骤七：将压花后的半成品表面涂上色彩，制成成品；步骤八：将所述成品晾干，收卷。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。