The invention discloses a fast one component moisture curable polyurethane adhesive and preparation method thereof, by Papi and ethylene glycol or polyethylene oxide / poly propylene oxide and three alcohol formulation was prepared; the do A Kakido polyphenyl isocyanate and poly oxide ethylene glycol and / or polyoxypropylene alcohol by three the reaction molar ratio formula, or Papi according to the reaction mole ratio than ethylene glycol or polyethylene oxide / poly propylene oxide and three alcohol in excess of 1 to 2 times. The invention of steam pressure is small, low toxicity, no harm to human body or environment, improve the basic organic volatiles, energy consumption and dissimilar materials bonding problems, significantly reducing the cost, is a kind of environmental friendly polyurethane adhesive performance; the invention has 30 minutes to deliver rubber material, it has the shear strength and impact the chemical characteristics of excellent adhesion, good adhesion, suitable for all kinds of structural domain.
【技术实现步骤摘要】
本专利技术涉及聚氨酯胶黏剂
，具体说是一种可交接生材的单组份快速湿固化聚氨酯胶黏剂及其制备方法，属林业工程中的木材科学与工程
技术介绍
鉴于当前木材加工原料结构的根本性变化，且伴随人们环保意识的增强和对生活质量要求的提高，本着对速生小径木、优质珍贵树种间伐材等的高效利用，同时满足人们对环境友好型胶黏剂以及降低木质材料胶接制品生产成本的需要和目的，开发研制环保型、价格低廉、能胶接高含水率木质材料的木材加工用合成树脂胶黏剂以及对新的加工技术与方法的探索，是木质材料胶接用胶黏剂和胶接技术方面一个亟待解决的新课题。目前应用于木材加工工业的聚氨酯胶黏剂主要原料就是异氰酸酯，其主要化学反应为:异氰酸酯与醇类化合物的反应生成聚氨酯。目前最常用的异氰酸酯是甲苯二异氰酸酯(TDI)和二苯基甲烷二异氰酸酯(MDI)。这种胶黏剂存在如下问题:①甲苯二异氰酸酯与二苯基甲烷二异氰酸酯具有一定的毒性，会对生成人员及环境产生危害。②生产时需要控制被胶接材料的含水率范围，增加生产成本且磨损刀具。③异种材料复合胶接困难。
技术实现思路
本专利技术的目的是针对上述不足，提供一种以多亚甲基多苯基多异氰酸酯(PAPI)为主要原料，提供一种可快速胶接生材的单组分湿固化聚氨酯胶黏剂及其制备方法。实现本专利技术目的的技术方案是:胶黏剂的配方包括:按反应摩尔配比的多亚甲基多苯基多异氰酸酯(PAPI)和聚氧化乙二醇(PEG)或/和聚氧化丙烯三醇，多亚甲基多苯基多异氰酸酯份量也可以按反应摩尔比比多元醇羟基过量I 2倍。该胶黏剂的配方中还包括增塑剂、添加剂、溶剂、催化剂。所述的增塑剂为领苯二甲酸...
【技术保护点】
一种单组份快速湿固化聚氨酯胶黏剂，其特征在于：所述胶黏剂是由多亚甲基多苯基多异氰酸酯和聚氧化乙二醇或/和聚氧化丙烯三醇的配方反应制得的；其中多亚甲基多苯基多异氰酸酯与聚氧化乙二醇或/和聚氧化丙烯三醇按反应摩尔配比配方，或者多亚甲基多苯基多异氰酸酯按反应摩尔比配比比聚氧化乙二醇或/和聚氧化丙烯三醇过量1～2倍。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。