The invention relates to a method for purifying the low grade magnesite by hydration, which takes low grade magnesite as raw material, and is calcined at 600 to 1000 DEG C, so that the magnesite is fully decomposed. The magnesium hydroxide after hydration of grinding and sieving, the characteristics of hydration of magnesium hydroxide powder and easy separation with other mineral impurities, removing impurities including calcium oxide, silicon oxide, alumina and ferric oxide with high hardness. The magnesium hydroxide is calcined at 600 to 900 DEG C for two times, and the purity of Magnesium Oxide is higher than 97.5%. By adopting the method of the invention, the low grade magnesite can be effectively utilized so as to make full use of it.
【技术实现步骤摘要】
本专利技术涉及矿物加工
，具体涉及。
技术介绍
我国菱镁矿资源丰富，分布广泛，目前的总探明储量约为34.02亿吨，居世界首位。然而，近年来，我国的生产厂家由于受生产成本和矿物加工技术水平的限制，往往只开采富矿，而开采过程中所产生的矿粉和低品位的矿石常常被当作废石堆积，造成了资源的极大浪费和环境的污染。且随着开采量的增加，特级菱镁矿已呈现逐步枯竭的趋势。因此，如何高效利用低品位的菱镁矿，提高菱镁矿资源的利用率，已经成为镁质材料行业的重要课题之一。关于低品 位菱镁矿的提纯方法，目前工业上主要采用浮选和化学提纯，浮选工艺设备投资大，工艺流程复杂，生产成本高，且需要使用浮选剂和大量的水资源，造成了环境的污染和水资源的浪费。化学提纯法的工艺流程更加复杂，工艺参数难于控制，生产过程中很难做到化学药剂的零排放，且生产成本高，因此，在工业生产中没有得到实质性的应用。专利技术专利200610134894.9提到一种菱镁矿的热选工艺，该工艺是以< 20mm粒度的菱镁矿贫矿为原料，在600 1000°C之间焙烧，并保温2s 150min，使原矿充分分解；然后对轻烧镁石进行自粉碎和筛分，把焙烧后硬度和强度存在差异的主矿物与含杂质矿物分开，以提高轻烧氧化镁粉纯度。该专利技术方法仅利用轻烧氧化镁与杂质间的硬度和强度差提纯，只能去除菱镁矿中的部分杂质。
技术实现思路
本专利技术提供了一种低品位菱镁矿水化提纯的新方法，克服了浮选和化学提纯工艺流程复杂，生产成本高，热选工艺产品纯度低的不足和缺点。该方法对低品位菱镁矿焙烧、水化、自磨、过筛、二次煅烧，将杂质与氧化镁分离，实现低品位...
【技术保护点】
一种低品位菱镁矿的水化提纯方法，其特征在于以低品位的菱镁矿为原料，采用水化的方法进行提纯，其工艺步骤包括焙烧、水化、自磨、过筛和二次煅烧，具体为：将菱镁矿原料放入反射炉、回转窑、悬浮炉、沸腾炉或隧道窑内于600～1000℃下充分焙烧；将轻烧后的氧化镁加水水化、自磨；将自磨后的氢氧化镁粉过筛，实现氢氧化镁和杂质的分离。最后将筛分后的氢氧化镁粉末于600～900℃二次煅烧，得到提纯轻烧氧化镁粉。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。