The present invention relates to an adhesive for lining hard rubber. A hot water curing adhesive for hard rubber lining, which is composed of a mixture of two components of a and B according to the weight of a 4:1: a natural rubber including: A, 100; B, C, 1~3 pigment; sulfur 20~40; D, Zinc Oxide 50~150; E, tackifying resin 15~40; F, G, DM1~3 promoter; mixed oil of 9332~5; h and 400~700 mixed solvent, the mixed solvent is toluene, xylene and gasoline in two or three; B: polyisocyanate solution. Pro before use, in accordance with the ratio in group A in B, mixing (at least 1 minutes, stirring) that use adhesive brushing. The adhesive of the present invention can be applied to hot water vulcanized lining hard rubber and has strong bonding strength.
【技术实现步骤摘要】
本专利技术涉及橡胶胶粘剂，尤其涉及一种衬里硬橡胶用的胶黏剂。
技术介绍
热水硫化衬里硬橡胶的特点是硫化温度低，且衬里泡在水中，在硫化前水对衬里 和其胶黏剂有较强的渗透性。现有的低温硫化用胶黏剂即自硫化胶黏剂，只有氯丁橡胶和 丁基橡胶两类，它们只适用于粘结软橡胶，而现有各类加热硫化胶黏剂粘结硬橡胶衬里，热 水硫化时，粘结强度达不到标准要求。
技术实现思路
本专利技术旨在解决上述缺陷，提供一种热水硫化衬里硬橡胶用的胶黏剂。本专利技术的 胶黏剂能适用于热水硫化的衬里硬橡胶，而且粘结强度大。本专利技术这样实现的一种热水硫化衬里硬橡胶用的胶黏剂，它包括； 甲组份(重量份数)天然橡胶100份 颜料Γ3份 硫磺20 40份 氧化锌5(Γ150份 增粘树脂15 40份 促进剂DM Γ3份 混合油933 2飞份 混合溶剂40(Γ600份； 乙组份聚异氰酸酯。所述混合溶剂为甲苯、二甲苯、汽油中的二种或三种。使用前按比例将乙组份加到甲组份中，并搅拌均勻(至少1分钟)，即可制得本专利技术 的胶黏剂。配比甲组份100，乙组份广4份(重量份)所述的胶黏剂的制备方法，包括甲组份混炼胶的制备将a g物料称量好后，在开炼机机或密炼机上炼胶，混合均勻并 在开炼机上压出广IOmm的橡胶片，冷却后切成小片；甲组份的制备将上述已切成小片的混炼胶加入高速搅拌机中，按比例加入配方中的 第h项，搅拌均勻即得甲组份；胶黏剂的配制使用前按比例将乙组份加到甲组份中，并搅拌均勻(至少1分钟)，即可 制得本专利技术的胶黏剂。配比甲组份100，乙组份广4份(重量份)本专利技术的胶黏剂能适用于热水硫化的衬里硬橡胶，而...
【技术保护点】
１．一种热水硫化衬里硬橡胶用的胶黏剂，其特征在于，它是由甲、乙两组份组成的混合物：甲组份包括下列组分：ａ、天然橡胶 １００份ｂ、颜料 １～３份ｃ、硫磺２０～４０份ｄ、氧化锌 ５０～１５０份ｅ、增粘树脂 １５～４０份ｆ、促进剂 ＤＭ １～３份ｇ、混合油 ９３３ ２～５份ｈ、混合溶剂 ４００～７００份所述混合溶剂为甲苯、二甲苯、汽油中的二种或三种；乙组份包括：聚异氰酸酯溶液甲组份，乙组份配比为：１００份： １～４份所述份数为重量份数。
【技术特征摘要】
【专利技术属性】
技术研发人员：彭高桥，程广来，梅杨敏，
申请(专利权)人：上海双浦橡胶防腐衬里有限公司，
类型：发明
国别省市：31