天然高分子一羟基磷灰石二级三维网络结构骨组织工程支架材料及其籽晶诱导制备方法技术

本发明专利技术公开了一种天然高分子一羟基磷灰石二级三维网络结构骨组织工程支架材料及其制备方法，是将羟基磷灰石纳米棒与天然高分子混合利用无毒交联剂京尼平进行交联，以冷冻干燥制备带有纳米籽晶的天然高分子多孔支架，再利用模拟体液进行生物矿化，在籽晶诱导下在具有微米级三维网络结构的天然高分子支架孔道壁上形成一层羟基磷灰石纳米三维网络结构。本发明专利技术的天然高分子一羟基磷灰石二级三维网络结构骨组织工程支架材料不但有很好的生物相容性，而且无毒且具备很高的生物活性，预示这类材料将在修复医学中具有广泛的应用前景。

Natural macromolecule hydroxyapatite two level three-dimensional network structure bone tissue engineering scaffold material and seed crystal induction preparation method thereof

The invention discloses a natural polymer hydroxyapatite two three-dimensional network structure of bone tissue engineering scaffold material and its preparation method, is a natural polymer mixed with hydroxyapatite nanorods using nontoxic genipin cross-linked natural polymer porous scaffolds by freeze-drying preparation with nano crystal seeds, and then use the simulated body fluid for biomineralization the seed, by forming a layer of nano hydroxyapatite three-dimensional network structure in the natural polymeric scaffold pore wall has a three-dimensional network structure on the micron level. The invention is a natural polymer hydroxyapatite two dimensional network structure of bone tissue engineering scaffold not only has good biocompatibility, nontoxic and have high biological activity, indicates that this kind of material has wide application prospect in repair medicine.

【技术实现步骤摘要】

【技术保护点】
１．一种天然高分子－羟基磷灰石二级三维网络结构骨组织工程支架材料，由天然高分子材料与纳米羟基磷灰石采用诱导模拟生物矿化的方法制得；其特征在于：所述支架ＥＥＥ材料由两级网络结构组成，一级结构为由天然高分子组成的三维网络结构，其壁厚为１－３微米，孔道直径为５０－１５０微米，二级结构为在一级结构孔道表面形成的由纳米羟基磷灰石组成的三维网络结构，其壁厚为２０－４０纳米，孔道直径为１００－１２０纳米；其中，所述天然高分子材料是壳聚糖或Ｉ型胶原蛋白，所述纳米羟基磷灰石是直径２０±５纳米、长度１２０±５０纳米的羟基磷灰石纳米棒，所述天然高分子材料与纳米羟基磷灰石复合的重量比例是４：１－２：１。

【技术特征摘要】

【专利技术属性】
技术研发人员：刘宏，王冠聪，赵洪石，任娜，陈丽梅，李建华，梁小萌，刘铎，江怀东，陶绪堂，王继扬，
申请(专利权)人：山东大学，
类型：发明
国别省市：88