The invention discloses a high-strength mulberry branch fiber PVC composite material. The weight ratio of components and components is: Plastic 55-60%, mulberry branch fiber 15-20%, titanium dioxide particles 4-6%, carbon black 3-5%, compatibilizer 10-15%, lubricant 6-9%, toughener 3-4%, mulberry branch fiber is modified by grafting. The further improvement lies in: adding corrosion resistance agent, components and components The weight ratio of the composite is 53-58% for plastics, 14-18% for mulberry branches, 4-6% for titanium dioxide particles, 3-5% for carbon black, 10-15% for compatibilizer, 6-9% for lubricant, 3-4% for toughener and 3-4% for corrosion resistance. The invention can significantly improve the compatibility of mulberry branch fiber and PVC.
【技术实现步骤摘要】
高强度桑枝纤维PVC复合材料
本专利技术涉及一种高分子复合材料，特别是一种PVC复合材料。
技术介绍
采用桑枝纤维与PVC复合制成桑枝纤维PVC复合材料可以有效利用桑枝纤维，但桑枝纤维与PVC相容性较差，影响了桑枝纤维PVC复合材料的性能。
技术实现思路
本专利技术针对现有技术的不足，提出一种能显著提高桑枝纤维与PVC相容性的高强度桑枝纤维PVC复合材料及其制备方法。本专利技术通过下述技术方案实现技术目标。高强度桑枝纤维PVC复合材料，组分及组分的重量配比为：塑料55～60％，桑枝纤维15～20％，钛白粉粒子4～6％，炭黑3～5％，相容剂10～15％，润滑剂6～9％，增韧剂3～4％；其改进之处在于：所述桑枝纤维进行接枝改性处理。进一步改进在于：添加耐腐蚀剂，组分及组分的重量配比为：塑料53～58％，桑枝纤维14～18％，钛白粉粒子4～6％，炭黑3～5％，相容剂10～15％，润滑剂6～9％，增韧剂3～4％，耐腐蚀剂3～4％。本专利技术与现有技术相比，具有以下积极效果：1、桑枝纤维进行接枝改性处理，解决桑枝纤维与PVC之间的界面相容性差和在塑料基体中的分散性差的问题。2、添加耐腐蚀剂，显著提高本专利技术耐腐蚀性能。具体实施方式下面结合实施例对本专利技术作进一步说明。实施例1：高强度桑枝纤维PVC复合材料，组分及组分的重量配比为：塑料55～60％，桑枝纤维15～20％，钛白粉粒子4～6％，炭黑3～5％，相容剂...
【技术保护点】
1.一种高强度桑枝纤维PVC复合材料，组分及组分的重量配比为：塑料55～60％，桑枝纤维15～20％，钛白粉粒子4～6％，炭黑3～5％，相容剂10～15％，润滑剂6～9％，增韧剂3～4％；其特征在于：所述桑枝纤维进行接枝改性处理。/n
【技术特征摘要】
1.一种高强度桑枝纤维PVC复合材料，组分及组分的重量配比为：塑料55～60％，桑枝纤维15～20％，钛白粉粒子4～6％，炭黑3～5％，相容剂10～15％，润滑剂6～9％，增韧剂3～4％；其特征在于：所述桑枝纤维进行接枝改性处理。