The invention relates to a tyre release agent, in particular to a tyre release agent, which comprises the following components: a tyre release agent, which comprises 15-25 parts by weight, 8-10 parts by polyethylene glycol, 10-20 parts by polysiloxane, 5-7 parts by paraffin, 11-15 parts by glycerol, 25-35 parts by dimethyl silicone oil and 2-4 parts by weight. The tire demoulding agent of the invention has strong stability, less coating amount in use, good durability of demoulding isolation, greatly reduces cost, saves man-hour, and improves production efficiency. The invention is convenient to use, simple to prepare, does not corrode the mould in the use process, does not pollute the mould easily, and has remarkable demoulding effect.
【技术实现步骤摘要】
一种轮胎脱模剂
本专利技术涉一种脱模剂,特别涉及一种轮胎脱模剂。
技术介绍
轮胎是汽车的重要配件之一,承载着汽车的所有重量,传送牵引和制动力,保证车轮与地面之间的附着力,缓冲外界的冲击。随着汽车行业的发展,对轮胎的性能要求也越来越高,轮胎在制作过程中,即在由模具对轮胎模制成型的过程中,不允许涂抹于模具上的脱模剂转移到轮胎的表面,因为脱模剂的化学成份易对轮胎产生影响,例如产生腐蚀作用,影响轮胎的使用寿命。现有的脱模剂性能不够稳定,脱模隔离不够持久,使用中较浪费时间,使用过程中容易沾污模具,脱模效果不明显。
技术实现思路
本专利技术克服了现有技术中的不足,提供了一种脱模效果较好的轮胎脱模剂。为了解决上述技术问题,本专利技术是通过以下技术方案实现的:一种轮胎脱模剂,按重量份数计,包括以下组份:硅酸钠15~25份、聚乙二醇8~10份、聚硅氧烷10~20份、石蜡5~7份、甘油11~15份、二甲基硅油25~35份、陶土2~4份。作为优选方案,按重量份数计,包括以下组份:硅酸钠20份、聚乙二醇9份、聚硅氧烷15份、石蜡6份、甘油13份、二甲基硅油30份、陶土3份。与现有技术相比,本专利技术的有益效果是:本专利技术的轮胎脱模剂具有较强的稳定性,使用中涂布量少,脱模隔离持久性好,大大降低了成本并节约了工时,提高了生产效率,本专利技术使用方便,制备方法简单,使用过程中不会腐蚀模具,不易污染模具,且脱模效果显著。具体实施方式下面结合具体实施方式对本专利技术作进一步详细描述:一种轮胎脱模剂,按重量份数计,包括以下组份:硅酸钠20份、聚乙二醇9份、聚硅氧烷15份、石蜡6份、甘油13份、 ...
【技术保护点】
1.一种轮胎脱模剂,其特征在于,按重量份数计,包括以下组份:硅酸钠15~25份、聚乙二醇8~10份、聚硅氧烷10~20份、石蜡5~7份、甘油11~15份、二甲基硅油25~35份、陶土2~4份。
【技术特征摘要】
1.一种轮胎脱模剂,其特征在于,按重量份数计,包括以下组份:硅酸钠15~25份、聚乙二醇8~10份、聚硅氧烷10~20份、石蜡5~7份、甘油11~15份、二甲基硅油25~35份、陶...
【专利技术属性】
技术研发人员:米佩彬,
申请(专利权)人:山东省三利轮胎制造有限公司,
类型:发明
国别省市:山东,37