The invention relates to a wear-resistant plastic bag, which is characterized in that the components of the said wear-resistant plastic bag are as follows: toluene diisocyanate 30 40 parts, polypropylene resin 20 30 parts, polyurethane resin 20 30 parts, zinc-aluminium alloy powder 10 15 parts, chitosan 5 10 parts, polyimide glass fiber 6 7 parts, silicon carbide 5 10 parts, 3 hydroxybenzoic acid 6 8 parts, polytetrad. Vinyl fluoride 1 2 phr, silica powder 0.5 1 phr, toughener 0.5 1 phr, curing agent 0.2 0.6 phr, cosolvent 0.2 0.5 phr and mildew inhibitor 0.5 1 phr. The wear-resistant plastic bag of the invention has high mechanical strength and high stability, strong corrosion resistance, good degradation effect, and will not affect the surrounding environment.
【技术实现步骤摘要】
一种耐磨塑料袋
本专利技术涉及塑料制品
,尤其涉及一种耐磨塑料袋。
技术介绍
塑料袋是人们日常生活中必不可少的物品,常用来承装其他物品,因其廉价、重量极轻、容量大、便于收纳的优点被广泛使用。塑料袋通常是以单体为原料,通过加聚或缩聚反应聚合而成的高分子化合物,它一般由合成树脂及其填料、增塑剂、稳定剂、润滑剂、色料等添加剂制作而成。在人们的日常生活中,塑料袋的应用非常广泛,但是废弃的塑料袋带来的“白色污染”也越来越严重。随着人们环保意识的增强,如何缓解白色污染已是人们日益关注的话题,越来越多的国家和地区已经限制塑料包装袋的生产、销售和使用。为落实科学发展观,建设资源节约型和环境友好型社会,人们开始从源头上采取有力措施,研究开发耐用耐磨的塑料袋,提高塑料袋的机械强度和耐腐蚀能力,延长塑料袋的使用时间和使用次数。
技术实现思路
为解决上述问题,本专利技术提供了一种耐磨塑料袋。本专利技术的技术方案如下:一种耐磨塑料袋,其特征在于:所述耐磨塑料袋的组分按照重量份如下所示:甲苯二异氰酸酯30-40份、聚丙烯树脂20-30份、聚氨酯树脂20-30份、锌铝合金粉10-15份、壳聚糖5-10份、聚酰亚胺玻璃纤维6-7份、碳化硅5-10份、3-羟基苯甲酸6-8份、聚四氟乙烯1-2份、硅石粉0.5-1份、增韧剂0.5-1份、固化剂0.2-0.6份、助溶剂0.2-0.5份和防霉剂0.5-1份。进一步的,所述增韧剂为聚乙烯醇缩丁醛、聚醚砜和聚苯醚酮中的一种或几种混合。进一步的,所述固化剂为二氨基二苯基砜、苯二甲胺三聚体中的一种。进一步的,所述助溶剂为对氨基苯甲酸、苯甲酸钠、乙酰胺中 ...
【技术保护点】
1.一种耐磨塑料袋,其特征在于:所述耐磨塑料袋的组分按照重量份如下所示:甲苯二异氰酸酯30‑40份、聚丙烯树脂20‑30份、聚氨酯树脂20‑30份、锌铝合金粉10‑15份、壳聚糖5‑10份、聚酰亚胺玻璃纤维6‑7份、碳化硅5‑10份、3‑羟基苯甲酸6‑8份、聚四氟乙烯1‑2份、硅石粉0.5‑1份、增韧剂0.5‑1份、固化剂0.2‑0.6份、助溶剂0.2‑0.5份和防霉剂0.5‑1份。
【技术特征摘要】
1.一种耐磨塑料袋,其特征在于:所述耐磨塑料袋的组分按照重量份如下所示:甲苯二异氰酸酯30-40份、聚丙烯树脂20-30份、聚氨酯树脂20-30份、锌铝合金粉10-15份、壳聚糖5-10份、聚酰亚胺玻璃纤维6-7份、碳化硅5-10份、3-羟基苯甲酸6-8份、聚四氟乙烯1-2份、硅石粉0.5-1份、增韧剂0.5-1份、固化剂0.2-0.6份、助溶剂0.2-0.5份和防霉剂0.5-1份。2.根据权利要求1所...
【专利技术属性】
技术研发人员:查辰,吴秀丽,
申请(专利权)人:常州中源工程技术有限公司,
类型:发明
国别省市:江苏,32