The invention relates to a production process of ionic safety glass film. It includes the following steps: (1) preparing master batch by using EVA resin with melting index of 2.5 5g/10min at 190 C, mixing with 1200 mesh fine calcium powder and using macromolecular wax as dispersant; (2) mixing master batch with EVA resin and coupling agent evenly, the melting index of EVA resin at 190 C is 25 40g/10min; (3) forming EVA glass adhesive by tape film forming process. The steps of the tablet. The invention provides a production process of ionic safety glass film. By using EVA material instead of traditional PVB material and adopting low temperature forming technology in the production process, the safety glass film can be glued with glass at lower temperature, thus forming the glued glass with high structural strength and safety.
【技术实现步骤摘要】
一种离子型安全玻璃胶片的生产工艺
本专利技术涉及一种离子型安全玻璃胶片的生产工艺。
技术介绍
在建筑装饰等领域，夹胶玻璃以其美观、坚固等优良特性得到了越来越广泛的应用，夹胶玻璃包括位于中心的玻璃胶片层和位于两侧的玻璃。安全玻璃是一款将玻璃胶片复合进两层玻璃中间，经高温高压胶合后，一体成型的夹层结构的新型特种玻璃产品。现有的安全玻璃胶片普遍结构强度不够，无法真正达到安全的目的，导致发生人身伤害。
技术实现思路
本专利技术为解决公知技术中存在的技术问题而提供一种离子型安全玻璃胶片的生产工艺，解决
技术介绍
中存在的问题。本专利技术为解决公知技术中存在的技术问题所采取的技术方案是：一种离子型安全玻璃胶片的生产工艺包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在2.5-5g/10min的EVA树脂，与1200目的精细钙粉相混合，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂在190℃时熔融指数在25-40g/10min；(3)采用流延成膜工艺生成EVA玻璃胶片的步骤。本专利技术的优点和积极效果是：本专利技术提供了一种离子型安全玻璃胶片的生产工艺，通过采用EVA材料代替传统的PVB材料、在生产过程中采用了低温成型工艺，制成的安全玻璃胶片能够在较低的温度下与玻璃夹胶，形成的夹胶玻璃结构强度高，安全性高。优选地：步骤(1)中所述的高分子蜡选取为聚乙烯蜡或者共聚酯蜡。优选地：步骤(2)中所述的偶联剂选取为氨乙基氨丙基三甲氧基硅烷或者氨乙基氨丙基甲基二甲氧基硅烷。具体实施方式为能进一步了解本专利技术的
技术实现思路
、特点及功效，兹...
【技术保护点】
1.一种离子型安全玻璃胶片的生产工艺，其特征是：包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在2.5‑5g/10min的EVA树脂，与1200目的精细钙粉相混合，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂在190℃时熔融指数在25‑40g/10min；(3)采用流延成膜工艺生成EVA玻璃胶片的步骤。
【技术特征摘要】
1.一种离子型安全玻璃胶片的生产工艺，其特征是：包括以下步骤，(1)制备母粒的步骤，母粒基材采用190℃时熔融指数在2.5-5g/10min的EVA树脂，与1200目的精细钙粉相混合，采用高分子蜡作分散剂；(2)将母粒与EVA树脂和偶联剂混合均匀的步骤，EVA树脂在190℃时熔融指数在25-40g/10min；(...