The present invention relates to a low temperature resistant plastic, which is mainly composed of 40 80 parts of polyamide, 30 50 parts of polypropylene, 10 20 parts of acrylate, 0.5 2.5 parts of sodium bicarbonate, 0.05 0.5 parts of cobalt octanate, 0.1 0.3 parts of phosphite chelating agent, 2 3 parts of polyolefin, 2 4 parts of glass fiber, 3 8 parts of ultra-fine calcium carbonate, 0.1 0.3 parts of defoamer and titanium white. Powder 0.1 0.5, glycerol 0.2 0.4, PU adhesive 0.2 0.5, light curing resin 5 15. The plastic of the invention has the advantages of good low temperature resistance and long service life in harsh outdoor environment.
【技术实现步骤摘要】
一种耐低温的塑料
本专利技术涉及新材料加工
，尤其涉及一种耐低温的塑料。
技术介绍
现有技术的塑料低温环境下容易发生脆裂，尤其是在户外的恶劣环境下其脆化过程非常短。
技术实现思路
为了解决上述技术问题，提供一种耐低温、不易在低温下脆裂的塑料，本专利技术提供以下技术方案：一种耐低温的塑料，由以质量份数计的以下成分组成：聚酰胺40-80份、聚丙烯30-50份、丙烯酸酯10-20份、碳酸氢钠0.5-2.5份、辛酸钴0.05-0.5份、亚磷酸酯螯合剂0.1-0.3份、聚烯烃2-3份、玻璃纤维2-4份、超细碳酸钙3-8份、消泡剂0.1-0.3份、钛白粉0.1-0.5份、丙三醇0.2-0.4份、PU胶黏剂0.2-0.5份、光固化树脂5-15份。进一步的，所述聚丙烯由聚乙烯代替。进一步的，所述超细碳酸钙的目数为160目。进一步的，所述钛白粉由稀土元素氧化物代替。进一步的，所述玻璃纤维由二烯丙基化合物代替。本专利技术的有益效果在于：通过配方的改善使得塑料的耐低温性能显著提高，能够在-40摄氏度的低温下保持1000h不脆裂。具体实施方式实施例1、一种耐低温的塑料，由以质量份数计的以下成分组成：聚酰胺60份、聚丙烯40份、丙烯酸酯15份、碳酸氢钠1.5份、辛酸钴0.25份、亚磷酸酯螯合剂0.2份、聚烯烃2.5份、玻璃纤维3份、超细碳酸钙5.5份、消泡剂0.2份、钛白粉0.3份、丙三醇0.3份、PU胶黏剂0.35份、光固化树脂10份。实施例2、一种耐低温的塑料，由以质量份数计的以下成分组成：聚酰胺40份、聚丙烯30份、丙烯酸酯10份、碳酸氢钠0.5份、辛酸钴0.1份、亚磷酸酯...
【技术保护点】
1.一种耐低温的塑料，其特征在于：由以质量份数计的以下成分组成：聚酰胺40‑80份、聚丙烯30‑50份、丙烯酸酯10‑20份、碳酸氢钠0.5‑2.5份、辛酸钴0.05‑0.5份、亚磷酸酯螯合剂0.1‑0.3份、聚烯烃2‑3份、玻璃纤维2‑4份、超细碳酸钙3‑8份、消泡剂0.1‑0.3份、钛白粉0.1‑0.5份、丙三醇0.2‑0.4份、PU胶黏剂0.2‑0.5份、光固化树脂5‑15份。
【技术特征摘要】
1.一种耐低温的塑料，其特征在于：由以质量份数计的以下成分组成：聚酰胺40-80份、聚丙烯30-50份、丙烯酸酯10-20份、碳酸氢钠0.5-2.5份、辛酸钴0.05-0.5份、亚磷酸酯螯合剂0.1-0.3份、聚烯烃2-3份、玻璃纤维2-4份、超细碳酸钙3-8份、消泡剂0.1-0.3份、钛白粉0.1-0.5份、丙三醇0.2-0.4份、PU胶黏剂0.2-0...
【专利技术属性】
技术研发人员：王云华，
申请(专利权)人：丹阳博亚新材料技术服务有限公司，
类型：发明
国别省市：江苏,32