A flame retardant composite material for automotive decorative panels is characterized in that: according to weight, the raw materials include: polycarbonate 40 80 parts, sodium hyphophosphite 0.5 5 parts, glass fiber 5 8 parts, plasticizer 2 8209 10 parts, titantitanium dioxide 1 8208 parts, antioxidant 1 8209 10 parts, triphenyl phosphate 5 8209 10 parts, phosphotriphenyl phosphate 5 8209 10 parts, compatibilizer 0.5 8209 5 parts, coupling agent 1 8209 5 parts, water 2 8209 parts, water 2 8209 parts, sepiolite 1 1, sepiolite 1 1 8209, sepioli 1, wheat rice stone 1 8209 2 2, wheat rice rice stone 1 The results of this study are as follows:1. Copies. The invention provides flame retardant composite materials for Automobile decorative panels with high impact strength, good mechanical strength and environmental protection.
【技术实现步骤摘要】
一种汽车装饰板用阻燃复合材料
本专利技术涉及汽车材料
，具体是一种汽车装饰板用阻燃复合材料。
技术介绍
目前，汽车上使用的装饰板主要为注塑件，其强度不够好，易发生变形、断裂，且还存在阻燃性能不佳等缺陷，在遇到事故时易引发火灾，从而造成严重的损失。
技术实现思路
根据上述缺陷，本专利技术的目的在于提供一种汽车装饰板用阻燃复合材料，提供抗冲击强度高、力学强度较好、环保的汽车装饰板用阻燃复合材料。本专利技术的技术方案是通过以下方式实现的：一种汽车装饰板用阻燃复合材料，其特征在于：按照重量份的原料包括：聚碳酸酯40-80份、次磷酸钠0.5-5份、玻璃纤维5-8、增塑剂2-10份、二氧化钛1-8份、抗氧剂1-10份、磷酸三苯酯5-10份、相容剂0.5-5份、偶联剂1-5份、水2-3份、海泡石1-2份，麦饭石1-2份。所述的偶联剂采用偶联剂KH560所述的汽车装饰板用阻燃复合材料，经过以下步骤制得：（1）、按照重量份分别称取原料：将聚碳酸酯、次磷酸钠、玻璃纤维、增塑剂、二氧化钛、抗氧剂、磷酸三苯酯、相容剂、偶联剂、水、海泡石、麦饭石分别称取；（2）、将上述称好的原料在高混机中混合均匀，送入双螺杆挤出机中，挤出、拉条、冷却、切粒后获得阻燃复合材料，高混机的转速为600-1500rpm；所述双螺杆挤出机各段螺杆温度为220-280℃。本专利技术的有益效果是：保证环保的前提下，提供抗冲击强度高、力学强度较好、汽车装饰板用阻燃复合材料。具体实施方式实施例1一种汽车装饰板用阻燃复合材料，按照重量份的原料包括：聚碳酸酯80份、次磷酸钠0.5份、玻璃纤维5、增塑剂2份、二氧化钛1...
【技术保护点】
1.一种汽车装饰板用阻燃复合材料，其特征在于：按照重量份的原料包括：聚碳酸酯40‑80份、次磷酸钠0.5‑5份、玻璃纤维5‑8、增塑剂2‑10份、二氧化钛1‑8份、抗氧剂1‑10份、磷酸三苯酯5‑10份、相容剂0.5‑5份、偶联剂1‑5份、水2‑3份、海泡石1‑2份，麦饭石1‑2份。
【技术特征摘要】
1.一种汽车装饰板用阻燃复合材料，其特征在于：按照重量份的原料包括：聚碳酸酯40-80份、次磷酸钠0.5-5份、玻璃纤维5-8、增塑剂2-10份、二氧化钛1-8份、抗氧剂1-10份、磷酸三苯酯5-10份、相容剂0.5-5份、偶联剂1-5份、水2-3份、海泡石1-2份，麦饭石1-2份。2.根据权利要求1所述的一种汽车装饰板用阻燃复合材料，其特征在于：所述的偶联剂采用偶联剂KH560。3.根据权...
【专利技术属性】
技术研发人员：范小伟，
申请(专利权)人：丹阳市亚美车辆部件有限公司，
类型：发明
国别省市：江苏,32