The present invention relates to an anti-aging rubber gasket. The components of the anti-aging rubber gasket are as follows: 15 25 parts of nitrile rubber, 15 20 parts of methyl vinyl silicone rubber, 20 25 parts of polycaprolactone, 5 10 parts of silicone powder, 3 7 parts of carbon black, 2 5 parts of basalt fiber, 1 2 parts of anti-aging agent, 0.5 1.5 parts of Polyaryl phosphate, 0.5 1.5 parts of antioxidant, and 1.5 parts of silicone powder. 1 3 phr of vulcanization accelerator. The invention has low production cost, good anti-aging effect, can effectively prolong the service life of rubber gaskets, improve the sealing performance of gaskets, and has broad application prospects.
【技术实现步骤摘要】
一种抗老化橡胶密封垫
本专利技术涉及橡胶密封垫
，尤其涉及一种抗老化橡胶密封垫。
技术介绍
橡胶密封垫为一种自膨胀密封垫片，属于管道密封部件。橡胶垫片具有耐油、耐酸碱、耐寒热、耐老化等性能，因此被广泛应用于汽车、电子、化工、抗静电、阻燃、食品等行业。虽然，目前的橡胶密封垫能够满足大部分生产和生活的需求，但是在高温的环境中，橡胶密封垫极易老化，并且极易变形进而使得橡胶密封垫的密封性能急剧下降，从而极大地降低了橡胶密封垫的密封性能。
技术实现思路
为解决上述问题，本专利技术提供了一种抗老化橡胶密封垫。本专利技术的技术方案如下：一种抗老化橡胶密封垫，其特征在于：所述抗老化橡胶密封垫的组分按照重量份如下所示：丁腈橡胶15-25份，甲基乙烯基硅橡胶15-20份，聚己内酯20-25份，硅微粉5-10份，炭黑3-7份，玄武岩纤维2-5份，抗老化剂1-2份，聚芳基磷酸酯0.5-1.5份，抗氧剂0.5-1.5份，硫化促进剂1-3份。进一步的，所述抗老化剂为硫代双甲基苯酚和硫代二丙酸双十八醇酯中的一种。进一步的，所述抗氧剂为二苯胺、对苯二胺中的一种。进一步的，所述硫化促进剂为乙烯硫脲、噻唑中的一种。借由上述方案，本专利技术至少具有如下优点：本专利技术制作成本低廉，抗老化效果好，能够有效延长橡胶密封垫的使用寿命，提高密封垫的密封性能，具有广阔的应用前景。具体实施方式下面结合实施例对本专利技术的技术方案作如下详细说明。实施例1一种抗老化橡胶密封垫，其特征在于：所述抗老化橡胶密封垫的组分按照重量份如下所示：丁腈橡胶20份，甲基乙烯基硅橡胶15份，聚己内酯25份，硅微粉7份，炭黑6...
【技术保护点】
1.一种抗老化橡胶密封垫，其特征在于：所述抗老化橡胶密封垫的组分按照重量份如下所示：丁腈橡胶15‑25份，甲基乙烯基硅橡胶15‑20份，聚己内酯20‑25份，硅微粉5‑10份，炭黑3‑7份，玄武岩纤维2‑5份，抗老化剂1‑2份，聚芳基磷酸酯0.5‑1.5份，抗氧剂0.5‑1.5份，硫化促进剂1‑3份。
【技术特征摘要】
1.一种抗老化橡胶密封垫，其特征在于：所述抗老化橡胶密封垫的组分按照重量份如下所示：丁腈橡胶15-25份，甲基乙烯基硅橡胶15-20份，聚己内酯20-25份，硅微粉5-10份，炭黑3-7份，玄武岩纤维2-5份，抗老化剂1-2份，聚芳基磷酸酯0.5-1.5份，抗氧剂0.5-1.5份，硫化促进剂1-3份。2....
【专利技术属性】
技术研发人员：陈云，
申请(专利权)人：丹阳市贝尔特橡塑制品有限公司，
类型：发明
国别省市：江苏,32