The invention relates to a layered molecular sieve and a preparation method thereof, which mainly solves the technical problems of a novel layered molecular sieve material not involved in the prior art. The present invention provides a new layered molecular sieve material, which contains the following chemical composition of molar ratio: 1SiO 2:(0-0.1) Al2O3:(0.1-0.3) Q:(1-10) H 2, in which template Q is a technical scheme of Gemini quaternary ammonium salt or quaternary amine base, which solves the above technical problems and obtains a new layered molecular sieve material, which can be used in industrial catalysis field.
【技术实现步骤摘要】
层状分子筛和其制备方法
本专利技术涉及一种层状分子筛和其制备方法,属于分子筛合成
技术介绍
沸石分子筛由于具有独特的孔道择形性、独特的固体酸性质以及优良的离子交换性质,因而应用非常广泛,在吸附,分离和催化等方面都已展现出了它们巨大的商业应用价值。比如在石油炼制和化工领域,Y沸石的应用给石油催化裂化技术带来了一场突跃性的革命,而其它分子筛催化剂,如ZSM-5沸石,丝光沸石,β沸石,MCM-22沸石,SAPO-34分子筛等的应用也给裂解、重整、异构化、芳烃歧化和烷基化、甲醇转化等等重要的石油炼制和化工技术带来了实质性的突破。鉴于分子筛在诸多工业领域中的重要作用,文献和专利中对于新分子筛的研究和新合成方法的研究一直都非常丰富。分子筛的来源主要有两个方面,一是从自然界矿物中得到,二是通过人工合成的办法获得,有些分子筛通过这两种途径都可以得到,但有些分子筛只能通过两者之一获得。但在石油炼制和化工领域,绝大多数的分子筛催化剂都是通过人工合成的办法来获得的。常用的分子筛人工合成方法是水热合成法,如ZSM-5【US3702886】,ZSM-11【US3709979】,ZSM-23【US4076842】,ZSM-35【US4016245】,Zeolitebeta【US3308069】,SAPO-34【US4440871】,MCM-22【US4954325】。使用水热法合成沸石分子筛一般是先通过硅源化合物,铝源化合物,碱,模板剂,和水等反应得到初始溶胶,然后该溶胶经过密闭体系下的水热反应得到晶化的分子筛产物。国内外学者通过研究发现沸石分子筛的催化性能通常与其形貌及孔 ...
【技术保护点】
1.一种层状分子筛,包含如下摩尔比的化学组成:1SiO2:(0~0.1)Al2O3:(0.01~0.4)Q:(1~10)H2O,其中模板剂Q为一种双子季铵盐或季胺碱,其结构由如下分子通式表示:
【技术特征摘要】
1.一种层状分子筛,包含如下摩尔比的化学组成:1SiO2:(0~0.1)Al2O3:(0.01~0.4)Q:(1~10)H2O,其中模板剂Q为一种双子季铵盐或季胺碱,其结构由如下分子通式表示:其中R1为H、卤素原子以及C1~C6的烃基中的至少一种,n取1~4整数,X选自卤素离子或氢氧根离子。2.根据权利要求1所述的层状分子筛,其特征在于所述的层状分子筛包含如下所示的X射线衍射数据:3.根据权利要求1所述的层状分子筛,其特征在于所述的R1为H、卤素原子以及C1~C6的烷基中的至少一种。4.根据权利要求1所述的层状分子筛,其特征在于所述的X选自OH—。5.权利要求1~4任一所述的层状分子筛的制备方法,包括如下几个步骤:a)按照1SiO2:(0~0.1)Al2O3:(0.01~1)Q:(20~200)H2O的初始摩尔配...
【专利技术属性】
技术研发人员:沈少春,杨为民,王振东,李应成,沙鸥,汪莹莹,
申请(专利权)人:中国石油化工股份有限公司,中国石油化工股份有限公司上海石油化工研究院,
类型:发明
国别省市:北京,11