The invention belongs to the field of building materials, and puts forward a kind of retarder for resin-bonded concrete. The raw materials include 25 35 parts of magnesium oxysulfide powder, 10 15 parts of building gypsum, 15 25 parts of epoxy resin, 10 20 parts of sodium borate, 5 15 parts of magnesium phosphate, 1 5 parts of calcium sucrose, 3 8 parts of lignin and 1 3 parts of sodium citrate by weight; improving the fluidity of concrete, controlling the slump loss, without any loss. As a result, the setting time is greatly prolonged and the cost-effective ratio is obvious; the weatherability, water resistance and alkali resistance of concrete products are improved; the manufacturing process is simple, and the raw materials are environmentally friendly and pollution-free.
【技术实现步骤摘要】
一种树脂胶混凝土缓凝剂
本专利技术属于建筑材料领域，具体涉及一种树脂胶混凝土缓凝剂。
技术介绍
混凝土缓凝剂是混凝土调凝剂的一种，延缓混凝土初凝和终凝时间而不影响混凝土后期强度。可单独使用，也可和减水剂等一起复配使用，具有一定的减水作用。作用为延缓水泥凝固，延长凝固时间，一般不影响混凝土质量，同减水剂一起使用时可提高减水率，超掺后可出现混凝土长时间不凝固现象，从而破坏混凝土质量。
技术实现思路
本专利技术的目的在于控制混凝土的塌落度和凝结时间，提出一种树脂胶混凝土缓凝剂。技术方案为实现上述专利技术目的，本专利技术提供了以下技术方案：一种树脂胶混凝土缓凝剂，原料按重量份包括：硫氧镁粉末25-35份，建筑石膏10-15份，环氧树脂15-25份，硼酸钠10-20份，磷酸镁5-15份，蔗糖钙1-5份，木质素3-8份，柠檬酸钠1-3份。本专利技术的有益作用在于：1.改善混凝土流动度，控制坍落度损失，又不会造成凝结时间的大幅延长，性价比优势明显。2.提高了混凝土产品耐候性，耐水性和耐碱性。3.制作工艺简单，原料环保无污染。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白易懂，下面结合具体实施例对本专利技术进一步详细说明，但本专利技术的内容完全不局限于此。实施例1一种树脂胶混凝土缓凝剂，原料按重量包括：硫氧镁粉末25Kg，建筑石膏10Kg，环氧树脂16Kg，硼酸钠11Kg，磷酸镁7Kg，蔗糖钙1Kg，木质素3Kg，柠檬酸钠1Kg。实施例2一种树脂胶混凝土缓凝剂，原料按重量包括：硫氧镁粉末33Kg，建筑石膏15Kg，环氧树脂19Kg，硼酸钠17Kg...
【技术保护点】
1.一种树脂胶混凝土缓凝剂，其特征在于，原料按重量份包括：硫氧镁粉末25‑35份，建筑石膏10‑15份，环氧树脂15‑25份，硼酸钠10‑20份，磷酸镁5‑15份，蔗糖钙1‑5份，木质素3‑8份，柠檬酸钠1‑3份。
【技术特征摘要】
1.一种树脂胶混凝土缓凝剂，其特征在于，原料按重量份包括：硫氧镁粉末25-35份，建筑石膏10-15份，环...