The invention belongs to the field of building materials, and puts forward a self-adhesive wear-resistant, waterproof and heat-insulating coil, which consists of (1) mung bean sand wear-resistant surface layer with particle size less than 20 mesh, (2) 1 mm thick petroleum asphalt, (3) 0.5 mm thick anti-corrosion aluminum foil layer, (4) 1.8 mm thick SBS modified asphalt waterproof coil, which is easy to lay and low in price, and is not necessary to be added when laying. Adhesive material can improve the paving speed and efficiency; rigid and flexible surface material can be double protected, wear-resistant and compressive, avoid material aging caused by direct sunlight, thus prolonging the service life of the material.
【技术实现步骤摘要】
一种自粘性耐磨防水隔热卷材
本专利技术属于建筑材料领域，具体涉及一种自粘性耐磨防水隔热卷材。
技术介绍
防水隔热卷材施工方便、工期短、成形后无须养护、不受气温影响、环境污染小，层厚容易按设计要求掌握，用材计算准确、施工现场管理方便，不易偷工减料，层厚均匀，空铺时能有效地克服基层应力。自粘性防水卷材一般用于屋面，地下室外墙、底板等，主要施工方法有干铺，湿铺，挂铺等。但卷材本身属于沥青橡胶类产品，对环境的适应性差，易老化后造成漏水现象的发生。
技术实现思路
本专利技术的目的在于提高自粘性防水隔热卷材的耐磨性，提出一种自粘性耐磨防水隔热卷材。技术方案为实现上述专利技术目的，本专利技术提供了以下技术方案：一种自粘性耐磨防水隔热卷材，自上而下依次包括（1）粒径不大于20目的绿豆砂耐磨表层，（2）1mm厚石油沥青，（3）0.5mm厚防腐铝箔层，（4）1.8mm厚SBS改性沥青防水卷材。本专利技术的有益作用在于：1.结构简单、铺设方便，且铺设价格低，便于推广使用。2.铺设时不需要加入粘黏材料，提高铺设速度和效率的效果。3.刚柔性表面材料双重保护，耐磨抗压，避免应阳光直射造成的材料老化，进而延长了材料的使用寿命。说明书附图图1是本专利技术的一种自粘性耐磨防水隔热卷材的一个具体实施例的结构示意图。图中附图标记的含义：（1）—粒径不大于20目的绿豆砂耐磨表层，（2）—1mm厚石油沥青，（3）—0.5mm厚防腐铝箔层，（4）—1.8mm厚SBS改性沥青防水卷材。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白易懂，下面结合具体实施例对本专利技术进一步详细...
【技术保护点】
1.一种自粘性耐磨防水隔热卷材，其特征在于，自上而下依次包括（1）粒径不大于20目的绿豆砂耐磨表层，（2）1mm厚石油沥青，（3）0.5mm厚防腐铝箔层，（4）1.8mm厚SBS改性沥青防水卷材。
【技术特征摘要】
1.一种自粘性耐磨防水隔热卷材，其特征在于，自上而下依次包括（1）粒径不大于20目的绿豆砂耐磨表层...