The invention discloses a preparation method of composite magnetic material adhesives, which is obtained by the following steps: firstly, water is heated to 45 70 C, starch is added under stirring conditions; then sodium silicate is added, dissolved sufficiently, cooled to room temperature, polyvinyl alcohol is added under ice bath conditions; finally, toluene sulfonic acid is added, and the adhesives prepared by the invention can be obtained after full mixing; So that the bonding strength of magnetic materials can be improved to obtain stable magnetic materials, which can improve the magnetic tensile properties of materials, high mechanical strength and wide application fields.
【技术实现步骤摘要】
一种复合磁性材料粘合剂的制备方法
本专利技术涉及一种材料，特别是一种复合磁性材料粘合剂的制备方法。
技术介绍
随着磁性材料在各种开关电源转换器，逆变器等通讯行业的广泛应用，越来越多的领域需要用到磁性材料，磁性材料的要求也就越来越高，电子整机系统向小型轻量化、平面贴装化等方向发展，开关电源的高频化是重要的技术途径，但现有的磁性材料稳定性不强，弹性和拉伸性很差，绿色、高效能的要求满足不了信息技术的需求。
技术实现思路
本专利技术的目的是提供一种复合磁性材料粘合剂的制备方法，该复合磁性材料粘合剂可以通过提高粘合强度，得到稳定性强的磁性材料，从而改善材料的磁性拉伸性，机械强度高，应用领域广阔。为实现上述目的，本专利技术的技术方案是：一种复合磁性材料粘合剂的制备方法，其特征在于，通过以下步骤获得：首先将水加热到45-70℃，搅拌条件下加入淀粉；随后加入硅酸钠，充分溶解后冷却至室温，在冰浴条件下加入聚乙烯醇；最后加入甲苯磺酸，充分混合后即可得到；其中各原料重量份数为：甲苯磺酸10-15份、硅酸钠20-30份、聚乙烯醇5-10份、淀粉3-8份、水40-50份。本专利技术的有益效果是：通过本专利技术制备出的粘合剂可以使使磁性材料的粘合强度有所提高得到稳定性强，得到稳定性强的磁性材料，从而改善材料的磁性拉伸性，应用领域广阔。具体实施方式下面对本专利技术作优选的详细说明：一种复合磁性材料粘合剂的制备方法，其特征在于，通过以下步骤获得：首先将，搅拌条件下加入淀粉；随后加入硅酸钠，充分溶解后冷却至室温，在冰浴条件下加入聚乙烯醇；最后加入甲苯磺酸，充分混合后即可得到；其中各原料重量份数...
【技术保护点】
1.一种复合磁性材料粘合剂的制备方法，其特征在于，通过以下步骤获得：首先将水加热到45‑70℃，搅拌条件下加入淀粉；随后加入硅酸钠，充分溶解后冷却至室温，在冰浴条件下加入聚乙烯醇；最后加入甲苯磺酸，充分混合后即可得到；其中各原料重量份数为：甲苯磺酸10‑15份、硅酸钠20‑30份、聚乙烯醇5‑10份、淀粉3‑8份、水40‑50份。
【技术特征摘要】
1.一种复合磁性材料粘合剂的制备方法，其特征在于，通过以下步骤获得：首先将水加热到45-70℃，搅拌条件下加入淀粉；随后加入硅酸钠，充分溶解后冷却至室温，在冰浴条件下...
【专利技术属性】
技术研发人员：王庆军，
申请(专利权)人：湖北汉耐尔新材料科技有限公司，
类型：发明
国别省市：湖北,42