The invention discloses a matte copper red lead-free metallic glaze and its preparation method. The glaze used in matte copper red lead-free metallic glaze contains the following components and the quality components of each component: potassium feldspar: 15 20 parts, albite: 10 15 parts, calcite: 5 10 parts, wollastonite: 7 10 parts, aluminium powder: 8 10 parts, zinc oxide: 10 15 parts, barium carbonate: 3 6 parts, copper oxide. 10 15 copies, nickel oxide: 0.5 1.2 copies, tungsten oxide: 1 2 copies. The glaze mask of the invention has extremely beautiful antique bronze color, high strength, wear resistance, low cost, and is suitable for a wide range of domestic and arts and crafts ceramics, so that customers can use it more assuredly.
【技术实现步骤摘要】
无光铜红色无铅金属釉及其制备方法
本专利技术涉及一种无光铜红色无铅金属釉及其制备方法。
技术介绍
目前，在瓷器行业中，瓷坯的造型是优质产品的基础，釉料的调配使瓷器更加绚丽多彩，同一造型的瓷坯，往往因釉面的不同，而对消费者的视觉产生不同的影响。
技术实现思路
本专利技术所要解决的技术问题是克服现有技术的缺陷，提供一种无光铜红色无铅金属釉，它的釉面具有极其美丽的仿古铜色，强度高，耐磨，造价低，适用广大日用瓷，工艺美术瓷，能让客户更放心使用。为了解决上述技术问题，本专利技术的技术方案是：一种无光铜红色无铅金属釉，它所使用的釉料含有的组分及各组分的质量份如下：钾长石：15-20份，钠长石：10-15份，方解石：5-10份，硅灰石：7-10份，铝粉：8-10份，氧化锌：10-15份，碳酸钡：3-6份，氧化铜：10-15份，氧化镍：0.5-1.2份，氧化钨：1-2份。本专利技术还提供了一种无光铜红色无铅金属釉的制备方法，方法的步骤中含有：S1：按照釉料的组分及各组分质量份备料；S2：按釉料：球：水的质量比＝1：1：1.6，湿法球磨15～18小时，球磨后的釉料过325目筛，再调成40～45波美度的釉浆；S3：取外表光洁的瓷器坯体浸入该釉浆后，经1200℃-1250℃的氧化气氛下烧制成品。采用了上述技术方案后，本专利技术的无光铜红色无铅金属釉的釉面具有极其美丽的仿古铜色，强度高，耐磨，造价低，适用广大日用瓷，工艺美术瓷，能让客户更放心使用。具体实施方式为了使本专利技术的内容更容易被清楚地理解，下面根据具体实施例，对本专利技术作进一步详细的说明。实施例一一种无光铜红色无铅金属釉...
【技术保护点】
1.一种无光铜红色无铅金属釉，其特征在于它所使用的釉料含有的组分及各组分的质量份如下：钾长石：15‑20份，钠长石：10‑15份，方解石：5‑10份，硅灰石：7‑10份，铝粉：8‑10份，氧化锌：10‑15份，碳酸钡：3‑6份，氧化铜：10‑15份，氧化镍：0.5‑1.2份，氧化钨：1‑2份。
【技术特征摘要】
1.一种无光铜红色无铅金属釉，其特征在于它所使用的釉料含有的组分及各组分的质量份如下：钾长石：15-20份，钠长石：10-15份，方解石：5-10份，硅灰石：7-10份，铝粉：8-10份，氧化锌：10-15份，碳酸钡：3-6份，氧化铜：10-15份，氧化镍：0.5-1.2份，氧化钨：1-2份。2.一种如权利要求1所...
【专利技术属性】
技术研发人员：徐柯，徐明良，
申请(专利权)人：醴陵市良盛陶瓷制造有限公司，
类型：发明
国别省市：湖南,43