The invention discloses a preparation process of antibacterial function titanium dioxide UV resin coating, which comprises the following steps: 1) adding surface modified titanium dioxide, n-butanol, pretreated methyl methacrylate (MMA) and surface modified graphene into the flask to mix fully; 2) raising the temperature in the flask to 70 C and cooling under the protection of nitrogen gas. However, the MMA-coated nano-TiO2/graphene prepolymer was obtained by filtration; 3) The initiator was added to the prepolymer, and the prepolymer film was coated on the surface of PVC floor, which was irradiated by ultraviolet light to produce a smooth surface of UV resin. The invention has bacteriostatic function.
【技术实现步骤摘要】
抑菌功能TiO2UV树脂涂层制备工艺
本专利技术涉及一种高分子复合材料领域，特别是一种UV树脂涂层制备工艺。
技术介绍
UV树脂涂层设置在PVC材料表面，可以使PVC材料耐磨，但如何使PVC材料具有抑菌功能，是一个研究课题。
技术实现思路
本专利技术针对现有技术的不足，提出一种具有抑菌功能的抑菌功能TiO2UV树脂涂层制备工艺。本专利技术通过下述技术方案实现技术目标。抑菌功能TiO2UV树脂涂层制备工艺，包括以下步骤：1）在烧瓶中加入表面改性过的TiO2、正丁醇、预处理过的甲基丙烯酸甲酯(MMA)，以及表面修饰过的石墨烯，充分搅拌；2）在氮气保护下使瓶内温度升至70℃，冷却、抽滤得到MMA包覆的纳米TiO2/石墨烯的预聚物；3）将引发剂加入到预聚物当中，并把该预聚物涂膜在PVC地板表面，经过紫外光的照射，使其发生辐射交联得到表面光滑的UV树脂。本专利技术与现有技术相比，具有以下积极效果：具有抑菌功能。具体实施方式下面结合实施例对本专利技术作进一步说明。抑菌功能TiO2UV树脂涂层制备工艺，包括以下步骤：1）在烧瓶中加入表面改性过的TiO2、正丁醇、预处理过的甲基丙烯酸甲酯(MMA)，以及表面修饰过的石墨烯，充分搅拌；2）在氮气保护下使瓶内温度升至70℃，冷却、抽滤得到MMA包覆的纳米TiO2/石墨烯的预聚物；3）将引发剂加入到预聚物当中，并把该预聚物涂膜在PVC地板表面，经过紫外光的照射，使其发生辐射交联得到表面光滑的UV树脂。
【技术保护点】
1.一种抑菌功能TiO2UV树脂涂层制备工艺，其特征在于：包括以下步骤：1）在烧瓶中加入表面改性过的TiO2、正丁醇、预处理过的甲基丙烯酸甲酯(MMA)，以及表面修饰过的石墨烯，充分搅拌；2）在氮气保护下使瓶内温度升至70℃，冷却、抽滤得到MMA包覆的纳米TiO2/石墨烯的预聚物；3）将引发剂加入到预聚物当中，并把该预聚物涂膜在PVC地板表面，经过紫外光的照射，使其发生辐射交联得到表面光滑的UV树脂。
【技术特征摘要】
1.一种抑菌功能TiO2UV树脂涂层制备工艺，其特征在于：包括以下步骤：1）在烧瓶中加入表面改性过的TiO2、正丁醇、预处理过的甲基丙烯酸甲酯(MMA)，以及表面修饰过的石墨烯，充分搅拌；2）在氮气保护...