The invention discloses a bamboo plate processing method, including the following process: cutting raw bamboo into bamboo slices, flattening bamboo slices to remove bamboo green bamboo yellow; S1.2: soaking the treated bamboo slices in antiseptic solution; S1.3: soaking the bamboo slices obtained from S1.2 in soybean oil under vacuum; S1.4: soaking S1. 3. The obtained bamboo slices are placed in organic solvents, soaked, removed and dried. According to the characteristics of bamboo itself, the invention adopts scientific methods to modify the bamboo in the production process of bamboo flooring to ensure the bamboo has good performance, corrosion resistance and durability, and greatly improves the stability of bamboo.
【技术实现步骤摘要】
竹板的加工方法
本专利技术涉及竹板的加工方法。
技术介绍
为了保护森林、防止水土流失追求以竹代木已成为大势所趋；竹要得到广泛应用必须制成竹板和竹钉的使用保障竹板不破裂才行，才能实现以竹代木的追求。现有的竹材由于加工方式方法存在不科学性，导致竹材耐腐蚀性差，在建材市场上消费者认知程度差。
技术实现思路
本专利技术的目的是克服现有产品中的不足，提供竹板的加工方法。为了达到上述目的，本专利技术是通过以下技术方案实现的：竹板的加工方法，包括以下工艺步骤：S1.1：将原竹切割为竹片，对竹片进行打平，去除竹青竹黄；S1.2：将处理后的竹片放入防腐液中浸泡，浸泡时间为5h，然后在常温环境下放置3天；所述防腐剂其原料成分以重量份计为五朵云21份、白醋21份、乙醇12份、藿香14份、桂皮19份、对羧基苯甲酸甲酯21份、山梨酸钾24份、丙二醇29份；S1.3：将S1.2获得的竹片在在真空条件下放入大豆油中进行加温浸泡，油温为177℃，浸泡时间为12h，将浸泡后的竹片捞出后，在竹片上下两面施压且在真空条件下静置，静置时间为7h，压力为2.8MPa；S1.4：将S1.3获得的竹片放置在有机溶剂中，浸泡47min，取出烘干，制得。本专利技术的有益效果如下：本专利技术很据竹材的自身性能特点，在竹地板生产过程中采用科学方法对竹材进行改性，保证竹材具有良好的性能，防腐耐用，极大的提高了竹材的稳定性。具体实施方式下面对本专利技术的技术方案作进一步说明：实施例1：竹板的加工方法，包括以下工艺步骤：S1.1：将原竹切割为竹片，对竹片进行打平，去除竹青竹黄；S1.2：将处理后的竹片放入防腐液中浸泡，...
【技术保护点】
1.竹板的加工方法，其特征在于，包括以下工艺步骤：S1.1：将原竹切割为竹片，对竹片进行打平，去除竹青竹黄；S1.2：将处理后的竹片放入防腐液中浸泡，浸泡时间为5h，然后在常温环境下放置3天；所述防腐剂其原料成分以重量份计为五朵云21份、白醋21份、乙醇12份、藿香14份、桂皮19份、对羧基苯甲酸甲酯21份、山梨酸钾24份、丙二醇29份；S1.3：将S1.2获得的竹片在在真空条件下放入大豆油中进行加温浸泡，油温为177℃，浸泡时间为12h，将浸泡后的竹片捞出后，在竹片上下两面施压且在真空条件下静置，静置时间为7h，压力为2.8MPa；S1.4：将S1.3获得的竹片放置在有机溶剂中，浸泡47min，取出烘干，制得。
【技术特征摘要】
1.竹板的加工方法，其特征在于，包括以下工艺步骤：S1.1：将原竹切割为竹片，对竹片进行打平，去除竹青竹黄；S1.2：将处理后的竹片放入防腐液中浸泡，浸泡时间为5h，然后在常温环境下放置3天；所述防腐剂其原料成分以重量份计为五朵云21份、白醋21份、乙醇12份、藿香14份、桂皮19份、对羧基苯甲酸甲酯21份、...