The invention discloses an anti stripping marble paint, which is composed of raw materials of the following weight parts: silicone acrylate emulsion 110, 140, zinc castor oil 1, 2, beta hydroxyalkyl amide 0.6, 1, twelve alkyl two methyl betaine 1 2, polyamide wax powder, 4, 4, butyl oleate, 2, and benzyl methane diisocyanate. The invention can effectively improve the dispersion compatibility between marble powder and wax powder. The marble paint of the invention has good surface hardness and peeling resistance, strong adhesion between film and substrate, and excellent comprehensive performance.
【技术实现步骤摘要】
一种抗剥离大理石漆及其制备方法
本专利技术属于漆领域,具体涉及一种抗剥离大理石漆及其制备方法。
技术介绍
大理石漆又称为仿大理石漆,仿大理石涂料等等,随着人们对装修工程的艺术追求,也随着天然石材,特别是优质量天然石材资源的逐渐枯竭,人工彩绘高仿真大理石,毫无疑问的成为了艺术涂料中,最有应用前景的一类产品.大理石与石材相比,具有以下特点:(1)易施工:与石材相比,仿大理石漆可以用于不同类型的墙面、柱面、顶面;(2)防护性:和真正的石材一样,防水,不受环境污染影响;(3)运输便利:比传统石材轻,容易运输;(4)颜色:多种颜色可供选择;(5)费用:产品的价格比天然大理石便宜70%。该产品主要成分是天然大理石粉,并且有大理石的效果。也正因为如此,真石漆、仿大理石漆的生产便成了建筑装饰领域的热门话题。近几年来,仿真石漆涂料面层在民用建筑外墙、室内装饰、以及园林塑石领域已经得到了广泛的应用,具有庄重、典雅、和谐和具有回归自然的感觉;然而,市售的大理石漆的黏度较低,抗剥离强度差,容易脱落。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足,提供一种抗剥离大理石漆及其制备方法。为实现上述目的,本专利技术采用以下技术方案:一种抗剥离大理石漆,它是由下述重量份的原料组成的:硅丙乳液110-140、蓖麻油酸锌1-2、β-羟烷基酰胺0.6-1、十二烷基二甲基甜菜碱1-2、聚酰胺蜡微粉4-6、油酸丁酯2-3、二苯基甲烷二异氰酸酯0.4-1、磷酸锆7-10、大理石粉10-12。一种抗剥离大理石漆的制备方法,包括以下步骤:(1)取聚酰胺蜡微粉,加入到其重量10-15倍的二甲基甲酰 ...
【技术保护点】
1.一种抗剥离大理石漆,其特征在于,它是由下述重量份的原料组成的:硅丙乳液110‑140、蓖麻油酸锌1‑2、β‑羟烷基酰胺0.6‑1、十二烷基二甲基甜菜碱1‑2、聚酰胺蜡微粉4‑6、油酸丁酯2‑3、二苯基甲烷二异氰酸酯0.4‑1、磷酸锆7‑10、大理石粉10‑12。
【技术特征摘要】
1.一种抗剥离大理石漆,其特征在于,它是由下述重量份的原料组成的:硅丙乳液110-140、蓖麻油酸锌1-2、β-羟烷基酰胺0.6-1、十二烷基二甲基甜菜碱1-2、聚酰胺蜡微粉4-6、油酸丁酯2-3、二苯基甲烷二异氰酸酯0.4-1、磷酸锆7-10、大理石粉10-12。2.一种如权利要求1所述的抗剥离大理石漆的制备方法,其特征在于,包括以下步骤:(1)取聚酰胺蜡微粉,加入到其重量10-15倍的二甲基甲酰胺中,送入到65-70℃的恒温水浴中,保温搅拌30-40分钟,出料,与蓖麻油酸锌混合,搅拌至...