The invention discloses an anti-microbial corrosion concrete admixture, which comprises the following weight components: cuprous oxide 20 40 phr, nitrate 30 40 phr, zinc 20 50 phr, sodium tripolyphosphate 1 2 phr, fiber 2 3 5 phr, hexamethylenetetramine 3 5 phr, active mineral admixture 90 phr phr and active activator 3.5 7.5 phr. Calcium nitrite 2 3, calcined gypsum 15 20 and bactericide 2 10 are applied by directly mixing the concrete with the special microbial bactericide with good germicidal efficacy and dispersing property, and it will not cause great pollution to the environment. Adding Bactericides to concrete or its protective coatings can kill or inhibit the reproduction of sulfur-oxidizing bacteria by combining the enzymes needed for their metabolism. The purpose of corrosion prevention can be achieved by controlling the formation of biological sulfuric acid.
【技术实现步骤摘要】
一种抗微生物腐蚀的混凝土外加剂
本专利技术涉及建筑材料
，尤其涉及一种抗微生物腐蚀的混凝土外加剂。
技术介绍
混凝土是现代应用最广泛的建筑材料，其具有原料丰富、价格低廉、工艺简单、强度高、耐久性好等优点。预拌混凝土是混凝土的一种，是指由水泥、集料、水以及根据需要掺入的外加剂、矿物掺合料等组分按一定比例在搅拌站经计量、拌制后出售的、并采用运输车在规定时间内运至使用地点的混凝土拌合物。混凝土外加剂是指在拌制混凝土的过程中掺入用以改善混凝土性能的物质。在制备混凝土时为了达到所需的效果通常需要加入各种外加剂，外加剂量的控制以及组分直接关系到混凝土的性能以及使用寿命。
技术实现思路
鉴于此，本专利技术提供了一种抗微生物腐蚀的混凝土外加剂，包含以下重量份的组分，氧化亚铜20-40份、硝酸盐30-40份、锌20-50份、三聚磷酸钠1-2份、纤维2-3份、六亚甲基四胺3-5份、活性矿物掺合料90-95份和活性激发剂3.5-7.5份、亚硝酸钙2-3份、煅烧石膏15-20份与杀菌剂2-10份。对本专利技术的进一步描述，所述煅烧石膏在600～800°C下煅烧得到。对本专利技术的进一步描述，所述氧化亚铜30份、硝酸盐30份、锌50份。采用上述技术方案，具有如下有益效果：通过在混凝土中直接掺入具有杀菌功效、分散性能好的高效混凝土专用微生物杀菌剂来应用，且不会对环境带来极大的污染。在混凝土或其保护涂层中掺入杀菌剂，杀菌剂可结合硫氧化细菌生命代谢所需的酶，从而杀灭或抑制其繁殖，通过控制生物硫酸生成达到腐蚀防治目的。具体实施方式一种抗微生物腐蚀的混凝土外加剂，包含以下重量份的组分，氧化...
【技术保护点】
1.一种抗微生物腐蚀的混凝土外加剂，其特征在于，包含以下重量份的组分，氧化亚铜20‑40份、硝酸盐30‑40份、锌20‑50份、三聚磷酸钠1‑2份、纤维2‑3份、六亚甲基四胺3‑5份、活性矿物掺合料90‑95份和活性激发剂3.5‑7.5份、亚硝酸钙2‑3份、煅烧石膏15‑20份与杀菌剂2‑10份。
【技术特征摘要】
1.一种抗微生物腐蚀的混凝土外加剂，其特征在于，包含以下重量份的组分，氧化亚铜20-40份、硝酸盐30-40份、锌20-50份、三聚磷酸钠1-2份、纤维2-3份、六亚甲基四胺3-5份、活性矿物掺合料90-95份和活性激发剂3.5-7.5份、亚硝酸钙2-3份...
【专利技术属性】
技术研发人员：张旋，
申请(专利权)人：徐州巨龙新材料科技有限公司，
类型：发明
国别省市：江苏,32