The present invention relates to a fast drying acrylic modified alkyd resin coating and its preparation process, which is characterized in that the acrylic modified alkyd resin is 55, 65, 15, 20, 15, 20, 3, 5, and 0.5 copies of the substrate wetting agent 0.5. Fumed silica 0.3, 0.5, solvent 4, 6, white paint special drier 0.8, 1.2, cobalt drier 0.2, 0.5, anti skinning agent 0.2, 0.4. It has excellent weatherability, water resistance, salt resistance and other properties, and the drying time has been greatly improved, the construction is excellent, suitable for engineering machinery, industrial facilities and other surface coating, and has excellent bonding with the base material.
【技术实现步骤摘要】
一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺
本专利技术所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，是一种速干型醇酸涂料，适用于工程机械，工业设施等表面的涂装，并与基材有优异的粘结性。
技术介绍
普通的醇酸树脂涂料，其干燥时间较长，影响施工周期，且涂料的耐候性也相对较差，长时间暴晒后，漆膜黄变性严重，因此研发出一款干燥时间短，耐候性优良，满足施工周期的醇酸涂料，符合当前涂料行业的现状。
技术实现思路
为解决上述技术问题，本专利技术所涉及的一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，按其质量分数比配制而成：丙烯酸改性醇酸树脂55-65份、钛白粉15-20份、沉淀硫酸钡15-20份、轻质碳酸钙3-5份、基材润湿剂0.3-0.5份、气相二氧化硅0.3-0.5份、溶剂4-6份、白漆专用催干剂0.8-1.2份、钴催干剂0.2-0.5份、防结皮剂0.2-0.4份。本专利技术所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，所使用的原材料沉淀硫酸钡目数为1250目。本专利技术所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，所使用的原材料轻质碳酸钙目数为1250目。本专利技术所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，所使用的原材料气相二氧化硅，具有良好的防沉降效果。本专利技术所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，所使用的原材料钛白粉为纳米级金红石钛白粉。本专利技术所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，所使用的原材料丙烯酸改性醇酸树脂，属于速...
【技术保护点】
1.本专利技术专利所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，按其原材料的质量分数比配制而成：丙烯酸改性醇酸树脂55‑65份、钛白粉15‑20份、沉淀硫酸钡15‑20份、轻质碳酸钙3‑5份、基材润湿剂0.3‑0.5份、气相二氧化硅0.3‑0.5份、溶剂4‑6份、白漆专用催干剂0.8‑1.2份、钴催干剂0.2‑0.5份、防结皮剂0.2‑0.4份。
【技术特征摘要】
1.本发明专利所涉及的是一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，按其原材料的质量分数比配制而成：丙烯酸改性醇酸树脂55-65份、钛白粉15-20份、沉淀硫酸钡15-20份、轻质碳酸钙3-5份、基材润湿剂0.3-0.5份、气相二氧化硅0.3-0.5份、溶剂4-6份、白漆专用催干剂0.8-1.2份、钴催干剂0.2-0.5份、防结皮剂0.2-0.4份。2.根据权利要求1所述的一种速干型丙烯酸改性醇酸树脂涂料及其制备工艺，其特征在于，所使用的原材料沉淀硫酸钡目数为1250目。3.根据权利要求1所述的一种速干型丙烯...