The invention belongs to the field of paper making and environmental protection, in particular to a recovery and utilization device for thick white water of paper making, including a tower body, an enzyme treatment layer and an adsorption layer. The enzyme treatment layer is arranged in the middle of the tower body to inoculate the medium with mixed bacteria, and the mixed bacteria are black Aspergillus niger and yeast with a ratio of 1:1.2 to 1.5, and the mixed bacteria are black. Aspergillus and yeast are able to grow and metabolize with nutrients in concentrated white water, produce pectinase, Chitanase, and cellulase to decompose colloid substances. The adsorbed layer is set in the lower part of the pagoda, including 20 ~ 30wt% attapulgite and 70 to 80wt% hydrotalcite, which is used to adsorb colored pollutants and anionic waste. Refuse. The invention also discloses the treatment method, which can eliminate the phenomenon of anionic garbage accumulation, improve the chemical environment in the processing, reduce the production cost, and effectively reduce the environmental pollution.
【技术实现步骤摘要】
造纸浓白水的回收利用装置及处理方法
本专利技术属于造纸和环保
,具体涉及一种造纸浓白水的回收利用装置及处理方法。
技术介绍
特种纸是将不同的纤维利用抄纸机抄制而成的具有特殊机能的纸张,特种纸在生产制造过程(抄制)中,会产生大量浓白水,其中含有大量的细小纤维和化工填料,若任其排放,则会造成极大的物质浪费和环境污染。因此,浓白水的回收再利用,是集节能、降耗、减排于一体的重要措施。目前,造纸企业多对浓白水进行封闭循环,以降低纤维浪费和环境污染,然而,随着白水的不断循环使用,其中的阴离子垃圾不断富集,令抄制工艺中的化学环境恶化,不但会与昂贵的阳离子化学助剂反应,造成资源浪费和经济损失,还会干扰纤维-纤维之间的相互作用、降低纸品质量(如白度、强度等),并附着在纸张上引起黑点、空洞等纸病,沉积在网部管道上影响生产效率。这给造纸工作者造成了长期的技术困扰,亟待解决。
技术实现思路
针对特种纸制造过程中存在的问题,本专利技术提供一种浓白水的回收利用装置及其方法,可杜绝阴离子垃圾富集的现象,改善抄制工艺中的化学环境,显著降低生产成本,有效降低环境污染。为解决上述问题,本专利技术通过以下技术方案实现:一种造纸浓白水的回收利用装置,包括塔体、酶处理层和吸附层,所述酶处理层设置在塔体中部,为接种有混合菌的培养基,所述混合菌为活菌个数比为1:1.2~1.5的黑曲霉和酵母菌,黑曲霉和酵母菌均能够借助浓白水中的营养物质进行生长代谢,产生果胶酶、壳聚糖酶和纤维素酶等,用于分解胶体物质;所述吸附层设置在塔体下部,包括20~30wt%的凹凸棒石和70~80wt%的水滑石,用于吸附有色污染物 ...
【技术保护点】
1.一种造纸浓白水的回收利用装置,其特征在于:包括塔体、酶处理层和吸附层,所述酶处理层设置在塔体中部,为接种有混合菌的培养基,所述混合菌为活菌个数比为1:1.2~1.5的黑曲霉和酵母菌;所述吸附层设置在塔体下部,包括20~30wt%的凹凸棒石和70~80wt%的水滑石;所述水滑石为人造水滑石,由以下步骤制成:(1)称取一定量的Al(NO3)3•9H2O和Mg(NO3)2•6H2O,分别加入蒸馏水中充分溶解,各配制成浓度为1.0mol•L‑1的溶液;(2)将所得溶液按体积比1:2加入容器中混合,并进行超声分散5min后,得到混合溶液A;(3)将混合溶液A持续进行搅拌和超声分散30min,同时滴加碱溶液,调节混合溶液pH值至10~11,得到混合溶液B;所述碱溶液为KOH或K2CO3溶液;(4)将混合溶液B进行离心分离5min得到沉淀,在所得沉淀中加入蒸馏水并进行超声分散10min,然后再进行离心分离3min,照本步骤前述操作反复进行,直至洗涤液为中性,得到沉淀C;(5)在所得沉淀C中加入乙醇,并进行超声分散10min,然后再进行离心分离5min,照本步骤前述操作反复3次,得到沉淀D;(6) ...
【技术特征摘要】
1.一种造纸浓白水的回收利用装置,其特征在于:包括塔体、酶处理层和吸附层,所述酶处理层设置在塔体中部,为接种有混合菌的培养基,所述混合菌为活菌个数比为1:1.2~1.5的黑曲霉和酵母菌;所述吸附层设置在塔体下部,包括20~30wt%的凹凸棒石和70~80wt%的水滑石;所述水滑石为人造水滑石,由以下步骤制成:(1)称取一定量的Al(NO3)3•9H2O和Mg(NO3)2•6H2O,分别加入蒸馏水中充分溶解,各配制成浓度为1.0mol•L-1的溶液;(2)将所得溶液按体积比1:2加入容器中混合,并进行超声分散5min后,得到混合溶液A;(3)将混合溶液A持续进行搅拌和超声分散30min,同时滴加碱溶液,调节混合溶液pH值至10~11,得到混合溶液B;所述碱溶液为KOH或K2CO3溶液;(4)将混合溶液B进行离心分离5min得到沉淀,在所得沉淀中加入蒸馏水并进行超声分散10min,然后再进行离心分离3min,照本步骤前述操作反复进行,直至洗涤液为中性,得到沉淀C;(5)在所得沉淀C中加入乙醇,并进行超声分散10min,然后再进行离心分离5min,照本步骤前述操作反复3次,得到沉淀D;(6)将沉淀D于100℃条件下烘干18h,然后,将烘干物打碎成颗粒状,即得水滑石前驱体E;(7)将前驱体E置于加热装置中,以10℃•min-1的升温速率加热至400℃保温2h,再以6℃•min-1的升温速率继续加热至900℃保温5h,然...