The invention relates to the field of polymer material technology, in particular to a high temperature resistant material for fire protection cables. This kind of fire resistant cable is made up of high temperature resistant material, consisting of three diethylene rubber 45~58 parts, silicone rubber 10~22 parts, ancient Malone resin 10~16, phenolic resin 4~10, diatomite 12~20, clay 2~6, sepiolite 1~8, polyethylene wax 1~6, four zirconium fluoride 4~9, polyacrylamide 3~10. Parts, Sijiqing 6~12 parts, carbon black 5~11 parts, carbon fiber 1~5 parts and nano Zinc Oxide 1~5 parts. This kind of fire-resistant cable has the advantages of reasonable proportioning of high temperature resistant materials, cheap and readily available raw materials, low production cost, high temperature resistance and long service life. One
【技术实现步骤摘要】
一种防火电缆用耐高温材料
本专利技术涉及高分子材料
，具体涉及一种防火电缆用耐高温材料。
技术介绍
目前，随着社会经济的发展，电线电缆用量迅速增长，对电缆的质量要求也不断提高。现有的电缆在加工过程中因选料不合理，导致电缆不能满足人们的使用需求，给人们的使用带来很大的问题，也存在安全隐患。
技术实现思路
本专利技术目的在于解决上述问题，提供了一种防火电缆用耐高温材料。为实现上述目的，本专利技术提供了一种防火电缆用耐高温材料，由如下按照重量份的原料组成：三元乙丙橡胶45~58份、有机硅橡胶10~22份、古马隆树脂10~16份、酚醛树脂4~10份、硅藻土12~20份、陶土2~6份、海泡石1~8份、聚乙烯蜡1~6份、四氟化锆4~9份、聚丙烯酰胺3~10份、四季青6~12份、炭黑5~11份、碳纤维1~5份和纳米氧化锌1~5份。所述防火电缆用耐高温材料，由如下按照重量份的原料组成：三元乙丙橡胶48~52份、有机硅橡胶13~19份、古马隆树脂11~15份、酚醛树脂6~9份、硅藻土15~18份、陶土3~5份、海泡石2~6份、聚乙烯蜡2~5份、四氟化锆5~8份、聚丙烯酰胺4~9份、四季青8~10份、炭黑7~10份、碳纤维2~4份和纳米氧化锌2~4份。所述防火电缆用耐高温材料，由如下按照重量份的原料组成：三元乙丙橡胶50份、有机硅橡胶16份、古马隆树脂12份、酚醛树脂8份、硅藻土16份、陶土4份、海泡石5份、聚乙烯蜡4份、四氟化锆6份、聚丙烯酰胺8份、四季青9份、炭黑8份、碳纤维3份和纳米氧化锌3份。本专利技术的有益效果：该种防火电缆用耐高温材料成分配比合理，原料廉价易得，...
【技术保护点】
1.一种防火电缆用耐高温材料，其特征在于，由如下按照重量份的原料组成：三元乙丙
【技术特征摘要】
1.一种防火电缆用耐高温材料，其特征在于，由如下按照重量份的原料组成：三元乙丙橡胶45~58份、有机硅橡胶10~22份、古马隆树脂10~16份、酚醛树脂4~10份、硅藻土12~20份、陶土2~6份、海泡石1~8份、聚乙烯蜡1~6份、四氟化锆4~9份、聚丙烯酰胺3~10份、四季青6~12份、炭黑5~11份、碳纤维1~5份和纳米氧化锌1~5份。2.根据权利要求1所述的防火电缆用耐高温材料，其特征在于，由如下按照重量份的原料组成：三元乙丙橡胶48~52份、有机硅橡胶13~19份、古马隆树脂1...
【专利技术属性】
技术研发人员：陈永军，曹中年，
申请(专利权)人：安徽华星电缆集团有限公司，
类型：发明
国别省市：安徽,34