The invention discloses a waterproof coating for construction, which consists of deionized water: 200 300 copies; high water absorptive resin: 5 10 copies; methyl methacrylate: 40 60 copies; pigment: 50 80 copies; butyl acrylate: 60 80; sodium bicarbonate: 1, 2; calcium chloride: 5 10; hydroxymethyl cellulose: cellulose: cellulose: cellulose The initiator: 0.5, 1, and all the above parts are of quality. Preferably, the deionized water is 260 parts, and the number of the deionized water is the mass fraction. Preferably, the methyl methacrylate is 50 parts, and the number is the mass fraction. The beneficial effect of the invention is that it can endure sunshine and rain for a long time, and has better water resistance and durability.
【技术实现步骤摘要】
一种建筑用防水涂料
本专利技术涉及一种建筑用防水涂料。
技术介绍
防水涂料经固化后形成的防水薄膜具有一定的延伸性、弹塑性、抗裂性、抗渗性及耐候性，能起到防水、防渗和保护作用，因其具有良好的温度适应性、操作简便、易于维修与维护，广泛应用于阳台、卫生间、浴室、厨房等的防水。现有的建筑用防水涂料虽然柔韧性和耐水性、耐久性比较好，但是，无法承受长时间的日照和雨淋，给使用带来诸多不便。
技术实现思路
针对上述问题，本专利技术提供一种建筑用防水涂料，可以长时间承受日照和雨淋，耐水性和耐久性更好。为实现上述技术目的，达到上述技术效果，本专利技术通过以下技术方案实现：一种建筑用防水涂料，其原料组成为：去离子水：200-300份；高吸水树脂：5-10份；甲基丙烯酸甲酯：40-60份；颜料：50-80份；丙烯酸丁酯：60-80份；碳酸氢钠：1-2份；氯化钙：5-10份；羟甲基纤维素：3-6份；引发剂：0.5-1份；上述份数均为质量份数。优选，所述去离子水为260份，份数为质量份数。优选，所述甲基丙烯酸甲酯为50份，份数为质量份数。优选，所述颜料为60份，份数为质量份数。优选，所述丙烯酸丁酯为70份，份数为质量份数。优选，所述羟甲基纤维素为5份，份数为质量份数。本专利技术的有益效果是：可以长时间承受日照和雨淋，耐水性和耐久性更好。具体实施方式下面结合具体的实施例对本专利技术技术方案作进一步的详细描述，以使本领域的技术人员可以更好的理解本专利技术并能予以实施，但所举实施例不作为对本专利技术的限定。一种建筑用防水涂料，其原料组成为：去离子水：200-300份；高吸水树脂：5-10份；甲...
【技术保护点】
一种建筑用防水涂料，其特征在于，其原料组成为：去离子水：200‑300份；高吸水树脂：5‑10份；甲基丙烯酸甲酯：40‑60份；颜料：50‑80份；丙烯酸丁酯：60‑80份；碳酸氢钠：1‑2份；氯化钙：5‑10份；羟甲基纤维素：3‑6份；引发剂：0.5‑1份；上述份数均为质量份数。
【技术特征摘要】
1.一种建筑用防水涂料，其特征在于，其原料组成为：去离子水：200-300份；高吸水树脂：5-10份；甲基丙烯酸甲酯：40-60份；颜料：50-80份；丙烯酸丁酯：60-80份；碳酸氢钠：1-2份；氯化钙：5-10份；羟甲基纤维素：3-6份；引发剂：0.5-1份；上述份数均为质量份数。2.根据权利要求1所述的一种建筑用防水涂料，其特征在于，所述去离子水为260份，份数为质量份数。...