The present invention relates to a cement tile adhesive, which comprises the following raw materials in parts by weight: 35 quartz sand 60 copies, 2 copies, 1 basalt fiber redispersible powder 1 3 copies, 2 copies, 0.5 carbon fiber SAP 0.5 0.8 copies, 30 copies, 25 emulsion 0.4, 0.2 film-forming agent defoaming agent 0.2 0.4. The non cement-based ceramic tile adhesive provided by the invention has strong cohesive force, high temperature resistance and flexibility, which is much higher than that of cement based products. It can effectively solve the problem of ceramic tile falling off when cement based products are bonded at high temperature and large deformation.
【技术实现步骤摘要】
一种非水泥基瓷砖粘合剂
本专利技术属于建筑材料领域，具体涉及一种非水泥基瓷砖粘合剂。
技术介绍
目前市场上的瓷砖粘合剂多为水泥基瓷砖粘合剂，水泥基瓷砖粘合剂为偏刚性产品，在某些特殊的场所使用，比如高温场所、震动较大的区域及基层变形较大时，存在一定的安全隐患。
技术实现思路
针对现有技术中瓷砖胶在高温、变形较大基层上粘结时容易出现瓷砖脱落的问题，本专利技术提供了一种非水泥基瓷砖粘合剂，具有高粘度、高韧性和耐高温性能。本专利技术是通过以下技术方案实现的：一种非水泥基瓷砖粘合剂，包括如下重量份数的原料：石英砂35-60份、玄武岩纤维1-2份、可再分散乳胶粉1-3份、碳纤维0.5-2份、保水剂0.5-0.8份、乳液25-30份、成膜助剂0.2-0.4份、消泡剂0.2-0.4份。进一步的，所述石英砂粒径为50-100目。进一步的，所述玄武岩纤维的单丝直径为5-20μm。进一步的，所述可再分散乳胶粉为醋酸乙烯酯与乙烯共聚胶粉。进一步的，所述保水剂为甲基羟乙基纤维素醚或者甲基羟丙基纤维素醚。进一步的，所述乳液为苯丙乳液。进一步的，所述成膜助剂为丙二醇丁醚或丙二醇甲醚醋酸酯。进一步的，所述消泡剂为聚硅氧烷类消泡剂。上述非水泥基瓷砖粘合剂制备时，将各原料混合在一起搅拌均匀即可。本专利技术提供的非水泥基瓷砖粘合剂，粘结力强，耐高温，柔韧性远远高于水泥基产品，可有效解决水泥基产品在高温、变形较大基层上粘结时容易出现瓷砖脱落的问题。而且，本专利技术的非水泥基瓷砖粘合剂中引入了玄武岩纤维组分，提高了瓷砖粘合剂的耐热胶黏强度和柔韧性。具体实施方式以下将结合实施例来详细说明本专利技术的实施...
【技术保护点】
一种非水泥基瓷砖粘合剂，其特征在于，包括如下重量份数的原料：石英砂35‑60份、玄武岩纤维1‑2份、可再分散乳胶粉1‑3份、碳纤维0.5‑2份、保水剂0.5‑0.8份、乳液25‑30份、成膜助剂0.2‑0.4份、消泡剂0.2‑0.4份。
【技术特征摘要】
1.一种非水泥基瓷砖粘合剂，其特征在于，包括如下重量份数的原料：石英砂35-60份、玄武岩纤维1-2份、可再分散乳胶粉1-3份、碳纤维0.5-2份、保水剂0.5-0.8份、乳液25-30份、成膜助剂0.2-0.4份、消泡剂0.2-0.4份。2.根据权利要求1所述的非水泥基瓷砖粘合剂，其特征在于，所述石英砂粒径为50-100目。3.根据权利要求1所述的非水泥基瓷砖粘合剂，其特征在于，所述玄武岩纤维的单丝直径为5-20μm。4.根据权利要求1所述的...
【专利技术属性】
技术研发人员：方杰敏，
申请(专利权)人：桂林市漓江机电制造有限公司，
类型：发明
国别省市：广西,45