The present invention discloses a kind of water soluble building powder coating comprises the following components: the weight ratio of water soluble resin 5 10 copies, 85 copies, 65 filler curing agent 22, 8 thickener 0.2 0.6 copies, 1 copies, 0.2 dispersant, defoaming agent 4 6 and 2 color 3 copies, the filler is one or more than two kinds of combination of barium sulfate, silica powder, titanium dioxide, three kinds of inorganic filler. The water-soluble building powder coating with the above formula has lower cost compared with the existing coating formulation, and the overall coating layer is stable after product spray molding, so it has good application prospects.
【技术实现步骤摘要】
一种水溶性建筑粉末涂料
本专利技术涉及粉末涂料领域,具体涉及一种水溶性建筑粉末涂料。
技术介绍
粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。现有技术中,其粉末涂料由聚酯树脂、封闭型异佛尔铜二异氰酸酯、安息香和二丁基锡二月桂酸酯组成,其缺点为物理学性能差、覆盖效果较差,易产生细泡,无法满足电器喷涂和表层保护。即现有的粉末涂料覆盖性能差,不能满足生产生活需要。
技术实现思路
本专利技术要解决的技术问题是克服上述不足,提供一种覆盖性能好的涂料配方。为了解决上述技术问题,通过以下技术方案得以实施:一种水溶性建筑粉末涂料,其特征在于,包括以下重量份配比的组分:水溶性树脂5-10份、填料65-85份、固化剂8-22份、增稠剂0.2-0.6份、分散剂0.2-1份、消泡剂4-6份和色母2-3份,所述填料为硫酸钡、硅微粉、钛白粉三类无机填料中的一种或两种以上的组合。作为本专利技术的进一步改进,水溶性建筑粉末涂料,包括以下重量份配比的组分:水溶性树脂6-8份、填料70-80份、固化剂10-20份、增稠剂0.3-0.4份、分散剂0.4-0.8份、消泡剂5份和色母2.5份。作为本专利技术的进一步改进,水溶性建筑粉末涂料,包括以下重量份配比的组分:水溶性树脂5份、填料65份、固化剂8份、增稠剂0.2份、分散剂0.2份、消泡剂4份和色母2份。作为本专利技术的进一步改进,水溶性建筑粉末涂料,包括以下重量份配比的组分:水溶性树脂10份、填料85份、固化剂22份、增稠剂0.6份、分散剂1份、消泡剂6份 ...
【技术保护点】
一种水溶性建筑粉末涂料,其特征在于,包括以下重量份配比的组分:水溶性树脂5‑10份、填料65‑85份、固化剂8‑22份、增稠剂0.2‑0.6份、分散剂0.2‑1份、消泡剂4‑6份和色母2‑3份,所述填料为硫酸钡、硅微粉、钛白粉三类无机填料中的一种或两种以上的组合。
【技术特征摘要】
1.一种水溶性建筑粉末涂料,其特征在于,包括以下重量份配比的组分:水溶性树脂5-10份、填料65-85份、固化剂8-22份、增稠剂0.2-0.6份、分散剂0.2-1份、消泡剂4-6份和色母2-3份,所述填料为硫酸钡、硅微粉、钛白粉三类无机填料中的一种或两种以上的组合。2.根据权利要求1所述的水溶性建筑粉末涂料,其特征在于,包括以下重量份配比的组分:水溶性树脂6-8份、填料70-80份、固化剂10-20份、增稠剂0...