The invention relates to a ductile cast iron with aluminum casting mold release agent, lubricity and excellent releasability, casting surface is smooth, the mechanism for water-based release agent has good film-forming properties at high temperature, and has good dispersion, on the surface of the mould is easy to form micron thin film lubrication. At the same time, the water based demoulding agent can rapidly reduce the temperature of the die relative to the graphite or oil base. In the demoulding, three cresol phosphate is selected as a polar pressure agent, which is the key component of the film formation, and the film is formed by chemical reaction with the surface of the book. Two methylethanolamine was added to the demoulding agent in order to reduce the problem of spray gun plugging when spraying this mold release agent.
【技术实现步骤摘要】
一种球墨铸铁模具用铸铝浇筑脱模剂
本专利技术涉及一种铸铝浇筑脱模剂。
技术介绍
铸造是一种古老的制造方法，在我国可以追溯到6000年前。随着工业技术的发展，铸件的质量直接影响着产品的质量。金属型铸造是用金属制作的铸造用中空铸型模具的现代工艺。金属型的铸型模具能反复多次使用，每浇注一次金属液，就获得一次铸件，寿命很长，生产效率很高。金属型的铸件不但尺寸精度好，表面光洁，而且在浇注相同金属液的情况下，其铸件强度要比砂型的更高，更不容易损坏。因此，在大批量生产有色金属的中、小铸件时，只要铸件材料的熔点不过高，一般都优先选用金属型铸造。在实际生产过程中，发现采用球墨铸铁模具进行铝制品浇筑时，采用石墨基脱模机，其效果不稳定，经常带来对铸件表面损失的问题。
技术实现思路
专利技术目的：针对上述现有技术，提出一种球墨铸铁模具用铸铝浇筑脱模剂，使其用于球墨铸铁模具进行铝制品浇筑时，具有良好的脱模性。技术方案：一种球墨铸铁模具用铸铝浇筑脱模剂，由如下质量份数的原料组成：氧化聚乙烯蜡25~30份白矿油5~10份磷酸三甲酚酯2~6份阴离子表面活性剂6~9份二甲基乙醇胺1~2份水300~350份。进一步的，所述阴离子表面活性剂为多缩氨基酸钠。有益效果：本专利技术的一种球墨铸铁模具用铸铝浇筑脱模剂，具有良好的润滑性及脱模性，铸件表面光滑，其具体机理为，水基脱模剂具有良好的高温成膜性能，同时具有良好的分散性，在模具表面容易形成微米级润滑薄膜。同时，水基脱模剂相对石墨基或油基能快速对模具进行降温。本脱模性中，选择磷酸三甲酚酯作为极压剂，其是成膜的关键成分，与经书表面发生化学反应生成薄膜。为...
【技术保护点】
一种球墨铸铁模具用铸铝浇筑脱模剂，其特征在于，由如下质量份数的原料组成：氧化聚乙烯蜡 25~30份白矿油 5~10份磷酸三甲酚酯 2~6份阴离子表面活性剂 6~9份二甲基乙醇胺 1~2份水300~350份。
【技术特征摘要】
1.一种球墨铸铁模具用铸铝浇筑脱模剂，其特征在于，由如下质量份数的原料组成：氧化聚乙烯蜡25~30份白矿油5~10份磷酸三甲酚酯2~6份阴离子表面活性剂...
【专利技术属性】
技术研发人员：张楠，周思扬，张翔，
申请(专利权)人：镇江佳鑫精工设备有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。