The invention relates to the technical field of plastic packaging, in particular to a high strength polyethylene film. The invention provides a high strength polyethylene film, its raw materials include high density polyethylene, low pressure polyethylene, linear polyethylene, grafted polyolefin, oxidized polyethylene wax, polyethylene glycol octyl phenyl ether, silicon carbide, two sulfosuccinic acid alkyl ester salt, calcium powder, Magnesium Oxide, three ethylhexyl hydrogen phosphate, three oxidation two antimony, coupling agent plasticizer, antioxidant, stabilizer, polyethylene film production, good stability, high mechanical strength, good corrosion resistance, high compressive strength, durable.
【技术实现步骤摘要】
一种高强度聚乙烯薄膜
本专利技术涉及印刷包装
，具体为一种高强度聚乙烯薄膜。
技术介绍
PE薄膜，即聚乙烯薄膜，是指用聚乙烯生产的薄膜。聚乙烯为典型的热塑性塑料，是无臭、无味、无毒的可燃性白色粉末。成型加工的PE树脂均是经挤出造粒的蜡状颗粒料，外观呈乳白色。其分子量在1万-l00万范围内。分子量越高，其物理力学性能越好，越接近工程材料的要求水平。但分子量越高，其加工的难度也随之增大。聚乙烯熔点为100-130℃，其耐低温性能优良。在-60℃下仍可保持良好的力学性能，但使用温度在80-110℃。聚乙烯化学稳定性较好，但是在大气、阳光和氧的作用下，会发生老化，变色、龟裂、变脆或粉化，丧失其力学性能。聚乙烯无臭，无毒，手感似蜡，具有优良的耐低温性能，化学稳定性好，能耐大多数酸碱的侵蚀，而且质轻，无毒，具有优越的介电性能。但是市场上的聚乙烯薄膜，因为工艺及组分的因素，在使用时存在很多的不足，普遍存在机械强度不够、易腐蚀、易损坏、抗压强度不高的的缺点，使用效果欠佳。
技术实现思路
针对现有技术中存在的上述问题，本专利技术提出的一种高强度聚乙烯薄膜，稳定性好，具有良好的机械强度，耐腐蚀，抗压强度高，使用时间长。本专利技术的目的可以通过以下技术方案实现：一种高强度聚乙烯薄膜，由下列重量份数的原料组成：高密度聚乙烯28～40份，低压聚乙烯15～28份，线性聚乙烯30～45份，接枝聚烯烃13～20份，氧化聚乙烯蜡6～12份，聚乙二醇辛基苯基醚4～8份，碳化硅8～15份，磺基琥珀酸二烷基酯盐5～10份，钙粉7～12份，氢氧化镁6～10份，三乙基己基磷酸13～18份，三氧化二...
【技术保护点】
一种高强度聚乙烯薄膜，其特征在于，由下列重量份数的原料组成：高密度聚乙烯28～40份，低压聚乙烯15～28份，线性聚乙烯30～45份，接枝聚烯烃13～20份，氧化聚乙烯蜡6～12份，聚乙二醇辛基苯基醚4～8份，碳化硅8～15份，磺基琥珀酸二烷基酯盐5～10份，钙粉7～12份，氢氧化镁6～10份，三乙基己基磷酸13～18份，三氧化二锑8～15份，偶联剂2～6份，增塑剂2～6份，抗氧剂4～8份，稳定剂2～5份，润滑剂1～3份。
【技术特征摘要】
1.一种高强度聚乙烯薄膜，其特征在于，由下列重量份数的原料组成：高密度聚乙烯28～40份，低压聚乙烯15～28份，线性聚乙烯30～45份，接枝聚烯烃13～20份，氧化聚乙烯蜡6～12份，聚乙二醇辛基苯基醚4～8份，碳化硅8～15份，磺基琥珀酸二烷基酯盐5～10份，钙粉7～12份，氢氧化镁6～10份，三乙基己基磷酸13～18份，三氧化二锑8～15份，偶联剂2～6份，增塑剂2～6份，抗氧剂4～8份，稳定剂2～5份，润滑剂1～3份。2.根据权利...
【专利技术属性】
技术研发人员：黄桂云，许焱，
申请(专利权)人：安徽省天乐塑业有限公司，
类型：发明
国别省市：安徽,34