A flame retardant paper honeycomb, which consists of the following parts by weight of raw material: nanometer calcium carbonate 3 12 weight, 4 6 nano silica weight, nanometer zinc borate 2 6 weight, two nano antimony oxide 3 5 weight portions, 1 2 nano aluminum hydroxide weight of deionized water, 50 150 weight. The present invention has no toxicity at room temperature, at high temperature and in paper burning does not emit toxic gases, generated only non combustible gas carbon dioxide CO2, and is easy to form a glass protective layer, thereby isolating the surface and prevents the flame in the combustion flame, paper, flame spread, suffocation; the formula of the invention can increase the paper the strength and rigidity, no moisture absorption, no decomposition, durable flame retardant, excellent performance, convenient popularization.
【技术实现步骤摘要】
一种用于纸蜂窝的阻燃剂及其制备方法
本专利技术涉及一种用于纸蜂窝的阻燃剂及其制备方法，属于纸张生产用化学品领域。
技术介绍
新型阻燃纸蜂窝轻质墙材作为一种符合国家宏观政策、产业发展方向，低碳环保、循环经济、可持续发展的新型建筑材料，具有强度高，整体性好，隔音隔热，阻燃防火，抗震防震，施工便捷，缩短工期，提高工效，减小劳动强度，增大空间使用面积、提高得房率，居住环保、清洁、舒适，其优异性日益彰显，越来越被广泛采用，其所用原料是阻燃纸。通常生产阻燃纸的阻燃剂主要是氮磷系列，卤素系列等，这类阻燃剂有良好的阻燃效果。但是这种阻燃剂有它严重缺点，易吸潮，阻燃后的纸张变软，强度下降。在光线下或长期暴露在空气中容易分解，阻燃性大大降低，甚至完全失去阻燃性。这就给出了阻燃纸蜂窝用阻燃纸难以逾越的难题。
技术实现思路
针对现有技术存在的不足，本专利技术所要解决的技术问题是，提供一种用于纸蜂窝的阻燃剂及其制备方法，可增加纸的强度和刚性，不吸潮，不分解，持久阻燃，无毒性，性能优异，便于推广。为解决上述技术问题，本专利技术采取的技术方案是，一种用于纸蜂窝的阻燃剂，其由以下重量份数的原料制成：纳米碳酸钙3-12重量份,纳米二氧化硅4-6重量份,纳米硼酸锌2-6重量份,纳米二氧化锑3-5，纳米氢氧化铝1-2重量份，水50-150重量份。优化的，上述新型阻燃纸蜂窝专用阻燃剂，其由以下重量份数的原料制成：纳米碳酸钙7重量份,二氧化硅5重量份,硼酸锌4重量份,二氧化锑4，氢氧化铝1重量份，水100重量份。一种权利要求1或2所述的一种用于纸蜂窝的阻燃剂的制备方法，其按权利要求1或2所述的重量份配...
【技术保护点】
一种用于纸蜂窝的阻燃剂，其特征在于 ：由以下重量份数的原料制成 ：纳米碳酸钙3‑12 重量份 , 纳米二氧化硅4‑6 重量份 , 纳米硼酸锌 2‑6 重量份 , 纳米二氧化锑3‑5重量份， 纳米氢氧化铝1‑2重量份，去离子水50‑150重量份。
【技术特征摘要】
1.一种用于纸蜂窝的阻燃剂，其特征在于：由以下重量份数的原料制成：纳米碳酸钙3-12重量份,纳米二氧化硅4-6重量份,纳米硼酸锌2-6重量份,纳米二氧化锑3-5重量份，纳米氢氧化铝1-2重量份，去离子水50-150重量份。2.根据权利要求1所述的一种用于纸蜂窝的阻燃剂，其特征在于：由以下重量份数的原料制成：纳米碳酸钙7重量份,纳米二氧化硅5重量份,纳米硼酸锌4重量份...
【专利技术属性】
技术研发人员：吴建平，南毅，陈信刚，孟维鑫，张健，钱寿俨，
申请(专利权)人：宝胜建设有限公司，
类型：发明
国别省市：江苏,32