The invention discloses a detection method for determining the harmonization of hard bitumen, which belongs to the technical field of road materials. The detection method for determining and reconciling hard bitumen is based on the conventional index analysis of asphalt, and through the combination of the flash point of volatile substances, the quality change of film oven and the penetration ratio index, we can judge whether the hard asphalt is used to blend asphalt. The detection method disclosed by the invention is highly operational and practical and simple, and it can be used to determine whether the hard asphalt is produced by the harmonic process through numerical comparison.
【技术实现步骤摘要】
一种判定调和硬质沥青的检测方法
本专利技术属于道路材料
，涉及一种调和硬质沥青的检测方法，尤其涉及一种判定针入度(25℃，0.1mm)在10-30的硬质沥青是否为调和硬质沥青的检测方法。
技术介绍
车辙是沥青路面病害的主要形式。硬质沥青因其质地硬、粘度大、劲度高，与石料的粘附性好，其硬质沥青混合料劲度模量高，整体高温稳定性好，具有良好的抗车辙能力，延长路面的使用寿命等特点，在国内高等级公路开始大规模的应用。目前硬质沥青的生产方法主要有蒸馏法、氧化法、溶剂脱沥青法和调和法。蒸馏法是原油经常减压装置分离出轻组分及蜡油组分，最终得到符合指标要求的硬质沥青。氧化法是在一定温度和一定通风量的情况下，使针入度较大的沥青在高温和氧气的作用下产生脱氢、氧化、聚合等一系列反应，最终得到硬质沥青。溶剂脱沥青法是采用轻烃作为溶剂，利用溶解度不同的原理将组分分离，得到硬质沥青。调和法是采用针入度大的沥青或油浆与超硬的沥青(包括湖沥青、岩沥青、脱油沥青、)或抗车辙剂等，通过计量调和搅拌，得到硬质沥青。采用直馏法、氧化法、溶剂脱沥青法生产的硬质沥青产品质量稳定，蒸发量小，高温抗车辙性、抗剪切力、抗疲劳性能好。而采用调和法生产的硬质沥青，产品质量不稳定，路用性能差，其缺点主要有以下几点：1、两种或两种以上不同产品调和，得到的硬质沥青产品质量不稳定，每批次产品指标波动较大；2、由于是轻、重组分的调和，在加热储存、运输、拌合过程中轻组分挥发量大，质量损失大；3、随着质量损失的增大，硬质沥青产品的性能发生变化；4、调和硬质沥青混合料路用性能差。
技术实现思路
为解决上述问题，本专利技术提供...
【技术保护点】
一种判定调和硬质沥青的检测方法，其特征在于：该方法基于沥青的常规指标分析，通过可挥发物质的闪点、薄膜烘箱质量变化、针入度比指标相结合，实现对硬质沥青是否为调和沥青做出判断；所述的硬质沥青，是指针入度(25℃，0.1mm)在10‑30的硬质沥青。
【技术特征摘要】
1.一种判定调和硬质沥青的检测方法，其特征在于：该方法基于沥青的常规指标分析，通过可挥发物质的闪点、薄膜烘箱质量变化、针入度比指标相结合，实现对硬质沥青是否为调和沥青做出判断；所述的硬质沥青，是指针入度(25℃，0.1mm)在10-30的硬质沥青。2.根据权利要求1所述的一种判定调和硬质沥青的检测方法，其特征在于该方法包括以下步骤：(1)采用克利夫兰开口闪点测定仪对硬质沥青样品进行检测分析，获取该样品的开口闪点数据；(2)采用薄膜烘箱试验，获取硬质沥青样品薄膜烘箱前后质量，通过计算得到硬质沥青样品的...