The invention discloses a cracking thermal insulation glazed hollow bead mortar comprises the following components: weight of Portland cement 30 40, heavy calcium carbonate powder 10 20 copies, 20 glass beads of 30 copies, 15 copies, 10 aggregate 5 moisture-proof anti crack materials 10, 5 probiotic powder 10, functional material 5 10. The invention of insulation mortar crack resistance can be overcome, insulation mortar cracking, shell and other defects, and high bonding strength, strong adhesion, good insulation, weather resistance, waterproof, fireproof and insulation performance of frost resistance; volume stability of mortar, condensation hardening volume expansion, not cracking, hollowing, water resistance, aging resistance, long service life.
【技术实现步骤摘要】
一种抗裂玻化微珠保温砂浆
本专利技术涉及一种保温砂浆,具体涉及一种抗裂玻化微珠保温砂浆,属于建筑领域。
技术介绍
目前,国家正在大力发展提倡环保、节能建筑结构。实施建筑节能必须大幅度提高维护结构,尤其是外墙的热工性能。一般来说,建筑维护结构采用节能方法主要有两种:一是直接选用保温墙体结构;二是选用在墙体外层涂刷一层保温砂浆。比较而言,采用墙体外层涂刷保温砂浆,施工简单,尤其是对于已有的建筑结构,其优势更加明显。因此,建筑物外墙采用粉刷保温砂浆以保证建筑物节能性能的方法得到越来越多地应用。保温砂浆是以各种轻质材料为骨料,以水泥为胶凝料,掺和一些改性添加剂,经生产企业搅拌混合而制成的一种预拌干粉砂浆,主要用于构筑建筑表面保温层的一种建筑材料,具有节能利废、保温隔热、耐老化的优异性能以及价格低廉、施工方便等特点,有着广泛的市场需求。目前市场上的保温砂浆种类繁多,性能参差不齐,大多数保温砂浆还是存在着抗裂性差的不足,容易出现开裂现象,不易在冬季施工、凝结硬化较慢、且与基材的粘结能力有限,在实际工程应用中受到一定的限制。
技术实现思路
本专利技术所要解决的技术问题是针对现有技术的不足,提供一种抗开裂性能优异的保温砂浆,可克服保温砂浆开裂、起壳等通病,且粘结强度高,附着力强,具有良好的保温隔热性、耐候性、防火防水性、抗冻性等性能。为了达到上述目的,本专利技术采用的技术方案是:一种抗裂玻化微珠保温砂浆,按照常规保温砂浆制备方法制备,包括以下重量份的组份:硅酸盐水泥30-40份、重质碳酸钙粉10-20份、玻化微珠20-30份、保温骨料10-15份、防潮抗裂材料5-10份、益生 ...
【技术保护点】
一种抗裂玻化微珠保温砂浆,按照常规保温砂浆制备方法制备,其特征在于,包括以下重量份的组份:硅酸盐水泥30‑40份、重质碳酸钙粉10‑20份、玻化微珠20‑30份、保温骨料10‑15份、防潮抗裂材料5‑10份、益生菌粉5‑10份、功能性材料5‑10份。
【技术特征摘要】
1.一种抗裂玻化微珠保温砂浆,按照常规保温砂浆制备方法制备,其特征在于,包括以下重量份的组份:硅酸盐水泥30-40份、重质碳酸钙粉10-20份、玻化微珠20-30份、保温骨料10-15份、防潮抗裂材料5-10份、益生菌粉5-10份、功能性材料5-10份。2.根据权利要求1所述的保温砂浆,其特征在于,所述的保温骨料为碳气凝胶,堆积密度为100—120kg/cm3。3.根据权利要求1所述的保温砂浆,其特征在于,所述的防...
【专利技术属性】
技术研发人员:张化夫,
申请(专利权)人:江苏特福特建材有限公司,
类型:发明
国别省市:江苏,32