The invention relates to a fireproof coating polyphenol glycidyl ether epoxy resin based on the material contained in the main group following quality parts: double (2,3 epoxycyclopentyl) ether resin 15 25 copies, 30 copies of the 15 metal hydroxide, ethanol 5 12 calcium carbonate, 7 10 copies. 15 talcum powder 25, polyphenol epoxy resin diglycidyl ether 6 12 copies, 8 copies of the 5 glass sand, resin 5 8. The invention uses double (2,3 epoxycyclopentyl) ether resin and metal hydroxides as composite, adding polyphenol glycidyl ether epoxy resin, the fireproof coating has flame retardant property, also can maintain the flame resistance, flame resistant and flame retardant fire resistance, can effectively protect the surrounding flammable materials.
【技术实现步骤摘要】
一种基于多酚环氧树脂的缩水甘油醚的防火涂料
本专利技术涉及一种防火涂料，具体涉及一种在室内防火用的聚有机酸系的防火涂料。
技术介绍
目前，国内外的防火措施从原理上来说分为疏导法和截流法，而截流法又分为外包封法、屏蔽法、喷涂法。防火材料作为一种涂覆在物体表面，具有隔热、防燃、阻燃功能的材料得到广泛应用，在建筑材料中使用可以有效延缓火势的发展，阻止火焰蔓延。申请公布号CN103923545A的专利申请公开了一种防火涂料，防火涂料配比，双氰胺、硅酸盐、季戊四醇、钛白粉、氯化石蜡、聚磷酸铵、丙烯酸乳液，其余为助剂，该防火涂料无毒、无刺激性，在涂覆时，粘结性好，美观而且阻燃效果好。现有的防火涂料往往还存在防火时间短，保护范围局限等缺点。进一步改善防火涂料的防火隔热效果仍然是本领域技术人员努力的方向。
技术实现思路
本专利技术所要解决的技术问题是针对上述现有技术提供一种基于多酚环氧树脂的缩水甘油醚的防火涂料，其具有良好的防火耐燃特性。本专利技术解决上述问题所采用的技术方案为：一种基于多酚环氧树脂的缩水甘油醚的防火涂料，其原料中包含如下质量份的主要组分：双（2,3-环氧环戊基）醚树脂15-25份，金属氢氧化物15-30份，乙醇5-12份，碳酸钙7-10份，滑石粉15-25份，多酚环氧树脂的缩水甘油醚6-12份，玻璃砂5-8份，树脂5-8份。本专利技术金属氢氧化物为氢氧化镁、氢氧化铝。本专利技术滑石粉的粒径为100～350nm。本专利技术玻璃砂可用玻璃纤维代替。本专利技术防火涂料还包括颜料、水、增稠剂、消泡剂。本专利技术防火涂料还包括流平剂、固化剂。与现有技术相比，本专利技术...
【技术保护点】
一种基于多酚环氧树脂的缩水甘油醚的防火涂料，其特征在于：其原料中包含如下质量份的主要组分：双（2,3‑环氧环戊基）醚树脂 15‑25份，金属氢氧化物 15‑30份，乙醇 5‑12份，碳酸钙 7‑10份，滑石粉 15‑25份，多酚环氧树脂的缩水甘油醚 6‑12份，玻璃砂 5‑8份，树脂 5‑8份。
【技术特征摘要】
1.一种基于多酚环氧树脂的缩水甘油醚的防火涂料，其特征在于：其原料中包含如下质量份的主要组分：双（2,3-环氧环戊基）醚树脂15-25份，金属氢氧化物15-30份，乙醇5-12份，碳酸钙7-10份，滑石粉15-25份，多酚环氧树脂的缩水甘油醚6-12份，玻璃砂5-8份，树脂5-8份。2.根据权利要求1所述的基于多酚环氧树脂的缩水甘油醚的防火涂料，其特征在于：所述金属氢氧化物为氢氧化镁、氢氧化铝。3.根据权利...
【专利技术属性】
技术研发人员：刘明贤，
申请(专利权)人：江阴市尤乐防火阻燃材料有限公司，
类型：发明
国别省市：江苏,32