The invention discloses a super hydrophobic nano coating and preparation method thereof, reactant weight percentages are as follows: TEOS 5 8 copies, 80 copies, 70 ethanol methyltriethoxysilane 0.01 0.2 copies, 10 copies, 5 distilled water containing fluorine coupling agent 0.3, 0.1 the catalyst 12 15. The invention has good superhydrophobic effect, and the production time is short, and the production efficiency is improved. After coating, the water droplet has a larger contact angle and a smaller rolling angle. In all types of material surface to achieve anti fingerprint, anti snow, anti frost, anti condensation, scratch resistant, water repellent, anti graffiti, easy to clean, smooth and delicate touch, enhance the antibacterial properties.
【技术实现步骤摘要】
超疏水纳米涂料及其制备方法
本专利技术涉及一种涂料,尤其是涉及一种超疏水纳米涂料及其制备方法。
技术介绍
人们将荷叶上不沾水、且水滴可以自己滚落的现象称为超疏水现象,将具有这种性质的表面称为超疏水表面。目前已有一些超疏水涂料生产,但是这些涂料生产时间较长,且形成的超疏水表面的接触角通常较小,而滚动角则过大。
技术实现思路
本专利技术为了克服上述的不足,提供了一种接触角大、滚动角小,且生产时间短的超疏水纳米涂料,包括如下重量百分比的反应物:正硅酸乙酯5-8份、无水乙醇70-80份、甲基三乙氧基硅烷0.01-0.2份、蒸馏水5-10份、含氟偶联剂0.1-0.3份、催化剂12-15份。本专利技术超疏水涂料的制备方法,包括以下步骤:(1)将重量份数为5-8份的正硅酸乙酯在容器中搅拌,并在搅拌的同时加入5-10份的蒸馏水、70-80份的无水乙醇和12-15份的催化剂,加热至70℃反应5-6h;(2)搅拌并加入0.01-0.2份甲基三乙氧基硅烷和0.1-0.3份的含氟偶联剂,保持70℃搅拌回流反应6-8h;(3)冷却,并调节pH;(4)加入无水乙醇稀释至固含量为25-35%,得到超疏水涂料。优选的,所述含氟偶联剂为十七氟癸基三甲氧基硅烷、十三氟辛基三乙氧基硅烷或十七氟癸基三乙氧基硅烷。优选的,所述催化剂为乙酸或盐酸。优选的,步骤(3)中采用有机碱将pH值调至8.5-10,有机碱为甲醇钠或乙醇钾。本专利技术的有益效果是:本专利技术具有良好的超疏水效果,而且生产时间短,提高了生产效率。涂料经涂布之后,对水滴具有较大的接触角和较小的滚动角。能在各类材料表面实现防指纹印、防积雪、 ...
【技术保护点】
一种超疏水纳米涂料,其特征在于,包括如下重量百分比的反应物:正硅酸乙酯 5‑8份无水乙醇 70‑80份甲基三乙氧基硅烷 0.01‑0.2份蒸馏水 5‑10份含氟偶联剂 0.1‑0.3份催化剂 12‑15份。
【技术特征摘要】
1.一种超疏水纳米涂料,其特征在于,包括如下重量百分比的反应物:正硅酸乙酯5-8份无水乙醇70-80份甲基三乙氧基硅烷0.01-0.2份蒸馏水5-10份含氟偶联剂0.1-0.3份催化剂12-15份。2.根据权利要求1所述的超疏水纳米涂料,其特征在于,所述含氟偶联剂为十七氟癸基三甲氧基硅烷、十三氟辛基三乙氧基硅烷或十七氟癸基三乙氧基硅烷。3.根据权利要求1所述的超疏水纳米涂料,其特征在于,所述催化剂为乙酸或盐酸。4.一种超疏水涂料的制备方法,其特征在于,包括以下步骤:(1)将重量份数为5-8份的正硅酸乙酯在容器中搅拌,并在搅拌的同时加入5-10份的蒸馏水、7...
【专利技术属性】
技术研发人员:吴立新,吴梓坚,郑坚,
申请(专利权)人:江阴市天邦涂料股份有限公司,
类型:发明
国别省市:江苏,32