The invention relates to a glass fiber reinforced PA66 materials by weight percentage, including raw material formula: PA66 50 90%, 5%, 1 compatilizer and stabilizer 0.1 lubricant 0.1 1% 0.5%, 20%, 5 flame retardant glass fiber 5 40%, 0.5%, 0.1 antioxidant coupling agent 0.5 1% the glass fiber reinforced PA66 composite material and the existing glass fiber reinforced PA66 composite material, product and heat resistance, toughness, resistance and excellent performance, can be widely used in the automotive industry, mechanical and electrical products, chemical engineering and other fields, and low manufacturing cost etc..
【技术实现步骤摘要】
一种玻纤增强PA66复合材料及其制备方法
本专利技术属于高分子材料加工
,具体涉及一种玻纤增强PA66复合材料及其制备方法,特别适用于制造汽车配件,电器配件等。
技术介绍
PA66(聚酰胺66或尼龙66),同PA6相比,PA66更广泛应用于汽车工业、仪器壳体以及其它需要有抗冲击性和高强度要求的产品。聚酰胺树脂,英文名称为polyamide,简称PA。俗称尼龙(Nylon),它是大分子主链重复单元中含有酰胺基团的高聚物的总称。为五大工程塑料中产量最大、品种最多、用途最广的品种。尼龙中的主要品种是尼龙6和尼龙66,占绝对主导地位,尼龙6为聚己内酰胺,而尼龙66为聚己二酰己二胺,尼龙66比尼龙6要硬l2%;其次是尼龙11,尼龙12,尼龙610,尼龙612,另外还有尼龙1010、尼龙46、尼龙7、尼龙9、尼龙13,新品种有尼龙6I、尼龙9T和特殊尼龙MXD6(阻隔性树脂)等,尼龙的改性品种数量繁多,如增强尼龙、单体浇铸尼龙(MC尼龙)、反应注射成型(RIM)尼龙、芳香族尼龙、透明尼龙、高抗冲(超韧)尼龙、电镀尼龙、导电尼龙、阻燃尼龙,尼龙与其他聚合物共混物和合金等,满足不同特殊要求,广泛用作金属,木材等传统材料代用品。
技术实现思路
为解决以上技术问题,本专利技术采取如下技术方案:一种玻纤增强PA66复合材料,以重量百分比计,其原料配方包括:PA6650-90%、相容剂1-5%、润滑剂0.1-1%、稳定剂0.1-0.5%、阻燃剂5-20%、玻纤5-40%、抗氧剂0.1-0.5%、偶联剂0.5-1.0%。所述的PA66为通用型尼龙。所述的相容剂为低分子量PA66接 ...
【技术保护点】
一种无浮纤玻纤增强PA66复合材料,以重量百分比计,其原料配方包括:PA66 50‑90%、相容剂1‑5%、润滑剂0.1‑1%、稳定剂0.1‑0.5%、阻燃剂5‑20%、玻纤5‑40%、抗氧剂0.1‑0.5%。
【技术特征摘要】
1.一种无浮纤玻纤增强PA66复合材料,以重量百分比计,其原料配方包括:PA6650-90%、相容剂1-5%、润滑剂0.1-1%、稳定剂0.1-0.5%、阻燃剂5-20%、玻纤5-40%、抗氧剂0.1-0.5%。2.一种玻纤增强PA66复合材料,根据权利要求1其特征在于:所述的PA66为通用型尼龙。3.一种玻纤增强PA66复合材料,根据权利要求1其特征在于:所述的相容剂为低分子量PA66接枝马来酸酐。4.一种玻纤增强PA66复合材料,根据权利要求1其特征在于:所述的润滑剂为金属皂类润滑剂、聚乙烯蜡类中一种或二种。5.一种玻纤增强PA66复合材料,根据权利要求1其特征在于:所述的稳定剂为无毒有机锡。6.一种玻纤增强PA66复合材料,根据权利要求1其特征在于:所述的阻燃剂为有机高分子阻燃剂。7.一种玻纤增强PA66复合材料,根据权利要求1其特征在...
【专利技术属性】
技术研发人员:缪汉叶,唐亚军,缪佳琳,
申请(专利权)人:东台晨霞新材料科技有限公司,
类型:发明
国别省市:江苏,32