The invention discloses a modified TPU film, with TPU particles as raw materials, including compatibility agent, bulking agent, flame retardant, natural polyphenols, epoxy resin and light stabilizer, the components by weight respectively: TPU particles 70 80, 3 6 compatibilizer, 1 filler 3 a flame retardant, 2 4 copies, 8 copies of the 5 natural polyphenols, epoxy resin 10 20 copies, 1.5 copies of the 0.5 light stabilizer. The invention has the advantages that the modified TPU film with high capacity, uniform thickness, high surface gloss, with hydrolysis, added natural polyphenol can enhance film yellowing resistance effectively, other components added, make the film more stable performance, suitable for the promotion of the use of.
【技术实现步骤摘要】
一种改性TPU薄膜
本专利技术涉及一种薄膜，尤其涉及一种改性TPU薄膜。
技术介绍
热塑性弹性体由于其优良的断裂伸长，回弹性，耐磨性，耐候性及比浇注聚氨酯优越的加工成型方法，而得到越来越广泛的应用。特别是由于聚氨酯行业的快速发展，又促进原料厂家的产能不断扩大，使得成本不断下降，从而促进新轮聚氨酯产品的应用开发。TPU薄膜具有韧性好、强度高、无味、无毒、可热合加工等特性，广泛应用于汽车工业、医疗卫生、生活用品等领域。TPU薄膜传统的生产工艺主要是流延，该工艺产能低，薄膜厚度不均匀，各功能改性助剂都需要先造粒再添加使用，使得生产成本极高，塑化不均匀，限制了TPU薄膜的推广应用。因此，为解决上述问题，特提供一种新的技术方案。
技术实现思路
本专利技术提供一种改性TPU薄膜。本专利技术采用的技术方案是：一种改性TPU薄膜，以TPU颗粒为原料，还包括相容剂、填充剂、阻燃剂、天然多酚、环氧树脂和光稳定剂，其组分按重量份计分别为：TPU颗粒70-80份，相容剂3-6份，填充剂1-3份，阻燃剂2-4份，天然多酚5-8份，环氧树脂10-20份，光稳定剂0.5-1.5份。优选地，所述天然多酚为茶黄素、茄红素、咖啡多酚、橄榄多酚或姜黄素。优选地，所述相容剂为ABS-g-MAH、PE-g-MAH或PP-g-MAH。优选地，所述填充剂为二氧化硅。本专利技术的有益效果是：该种改性TPU薄膜具有产能高、厚度均匀，表面光泽度高，同时具有水解性能，添加的天然多酚能有效的增强薄膜的耐黄性，其它组分的添加，使薄膜的性能更加稳定，适用于推广运用。具体实施方式为了加深对本专利技术的理解，下面将结合实施...
【技术保护点】
一种改性TPU薄膜，其特征在于：以TPU颗粒为原料，还包括相容剂、填充剂、阻燃剂、天然多酚、环氧树脂和光稳定剂，其组分按重量份计分别为：TPU颗粒70‑80份，相容剂3‑6份，填充剂1‑3份，阻燃剂2‑4份，天然多酚5‑8份，环氧树脂10‑20份，光稳定剂0.5‑1.5份。
【技术特征摘要】
1.一种改性TPU薄膜，其特征在于：以TPU颗粒为原料，还包括相容剂、填充剂、阻燃剂、天然多酚、环氧树脂和光稳定剂，其组分按重量份计分别为：TPU颗粒70-80份，相容剂3-6份，填充剂1-3份，阻燃剂2-4份，天然多酚5-8份，环氧树脂10-20份，光稳定剂0.5-1.5份。2.根据权利要求1...
【专利技术属性】
技术研发人员：倪程凯，
申请(专利权)人：苏州卡佩罗尔高分子材料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。