The invention discloses a high conductivity alloy wire, the high conductivity alloy wire comprises the following components in part by weight: aluminum, silicon, iron, copper, boron, titanium and rare earth elements; the rare earth element is composed of cerium and lanthanum, scandium, and the lanthanum, cerium and scandium in accordance with 14:6:1 the weight ratio of the mixed rare earth elements; each component into the furnace, melting and heating to heat at 750 780 DEG C, stirring until evenly stirring time is more than 30min, static insulation, obtained after casting alloy melt; Aluminum Alloy liquid Aluminum Alloy ingot, casting temperature control 690~700 C; induction heating, the temperature rose to 520~540 DEG C under the rolling temperature, rolling in the previous upgrade. The metal structure of the high conductivity alloy wire is obviously improved, and the tensile strength and elongation are greatly improved after the production test and the subsequent drawing, and the power consumption requirement of the stage and long time is also satisfied.
【技术实现步骤摘要】
高导电率合金线材
本专利技术涉及一种合金线材,尤其涉及一种高导电率合金线材。
技术介绍
合金线材是工业中使用最广泛的有色金属材料之一,在航空、航天、汽车、机械制造、船舶及化学工业中已有大量应用。随着科学技术以及工业经济的快速发展,铝合金的需求日益增多,铝合金的研究也随之深入。铝合金的广泛应用促进了铝合金在电力行业的发展,同时电力行业的发展有促进了铝合金的应用领域,现有技术,载流量相对普铝有一定提高,但不能较好的满足用电量较大或者阶段性的用电量较大的地区。
技术实现思路
本专利技术提供一种高导电率合金线材,此高导电率合金线材金属组织结构明显好转,经过生产试验以及后续拉丝时抗拉强度、伸长率大大改善,降低电阻率6~10%。为达到上述目的,本专利技术采用的技术方案是:一种高导电率合金线材,所述高导电率合金线材由以下重量份的组分组成:铝100份、硅0.04~0.045份、铁1~1.1份、铜0.18~0.22份、稀土元素0.08~0.1份、硼0.015~0.02份、钛0.01~0.012份;所述稀土元素由镧、铈和钪组成,且所述镧、铈和钪按照14:6:1重量份比例混合形成所述稀土元素;所述高导电率合金线材通过以下工艺获得,此工艺包括以下步骤:步骤一、将铝锭100份投入熔炉中,加热使之熔化并在750-780℃下保温,加入硅0.04~0.045份、铁1~1.1份、铜0.18~0.22份、稀土元素0.08~0.1份、硼0.015~0.02份和钛0.01~0.012份,充分搅拌至均匀,搅拌时间≥30min,静置保温,获得合金熔体;步骤二、在步骤一合金熔体加入精炼剂,并采用高纯氮气进 ...
【技术保护点】
一种高导电率合金线材,其特征在于:所述高导电率合金线材由以下重量份的组分组成:铝100份、硅0.04~0.045份、铁1~1.1份、铜0.18~0.22份、稀土元素0.08~0.1份、硼0.015~0.02份、钛0.01~0.012份;所述稀土元素由镧、铈和钪组成,且所述镧、铈和钪按照14:6:1重量份比例混合形成所述稀土元素;所述高导电率合金线材通过以下工艺获得,此工艺包括以下步骤:步骤一、将铝锭100份投入熔炉中,加热使之熔化并在750‑780℃下保温,加入硅0.04~0.045份、铁1~1.1份、铜0.18~0.22份、稀土元素0.08~0.1份、硼0.015~0.02份和钛0.01~0.012份,充分搅拌至均匀,搅拌时间≥30min,静置保温,获得合金熔体;步骤二、在步骤一合金熔体加入精炼剂,并采用高纯氮气进行精炼,氮气精炼温度750~780℃,再保温获得铝合金液;步骤三、将步骤二的铝合金液倾倒出炉,再经过在线除气系统进行除气,为了控制铝液内有害气体;步骤四、浇铸经过步骤三的铝合金液得到铝合金铸锭,浇铸过程控制浇铸温度690~700℃,控制浇铸速度5t/h,经过金相分析来确认结 ...
【技术特征摘要】
1.一种高导电率合金线材,其特征在于:所述高导电率合金线材由以下重量份的组分组成:铝100份、硅0.04~0.045份、铁1~1.1份、铜0.18~0.22份、稀土元素0.08~0.1份、硼0.015~0.02份、钛0.01~0.012份;所述稀土元素由镧、铈和钪组成,且所述镧、铈和钪按照14:6:1重量份比例混合形成所述稀土元素;所述高导电率合金线材通过以下工艺获得,此工艺包括以下步骤:步骤一、将铝锭100份投入熔炉中,加热使之熔化并在750-780℃下保温,加入硅0.04~0.045份、铁1~1.1份、铜0.18~0.22份、稀土元素0.08~0.1份、硼0.015~0.02份和钛0.01~0.012份,充分搅拌至均匀,搅拌时间≥30min,静置保温,获得合金熔体;步骤二、在步骤一合金熔体加入精炼剂,并采用高纯氮气进行精炼,氮气精炼温度75...
【专利技术属性】
技术研发人员:孟博,尹健,潘建,蔺亚强,王婧婧,
申请(专利权)人:江苏亨通电力特种导线有限公司,
类型:发明
国别省市:江苏,32