The invention discloses a building exterior wall decoration material, which comprises a fabric layer and a bottom layer, wherein, the material layer is made of cement, calcium silicate, asbestos and refined sand, and the bottom layer is made of cement, ceramsite and sand. In the invention, calcium silicate, ceramic components, has the characteristics of low coefficient of heat dissipation, thus greatly improves the insulation performance of brick, cement brick color in the fabric, it replaces the now on the outer surface of the building with Caiyouzhuan trouble, reduce the expenses, cost savings. Calcium silicate is used in the brick fabric, which has high strength and strong thermal insulation. The invention has the advantages of external heat insulation, internal heat preservation, external decoration and masonry wall, and can effectively save energy and reduce the building cost.
【技术实现步骤摘要】
本专利技术涉及建筑材料技术生产领域，特别是涉及一种建筑外墙装饰材料。
技术介绍
现有的建筑物外墙装饰大多采用粘土砖，其比重大、费用高，为了保温还要做一层保温层，为了美观还要在外墙上贴一层彩砖，这就使成本增大，增加人力和物力，且费时费力。
技术实现思路
本专利技术的目的在于提供一种建筑外墙装饰材料，完全可以替代传统的粘土砖，不仅可以使建筑物保温性能增强，而且美观耐用，并且可以防止高楼表层脱落的不安全因素。为实现上述技术目的，本专利技术采取的技术方案是：建筑外墙装饰材料，它包括面料层和底料层，所述面料层由彩色水泥、硅酸钙、石棉和精沙制成，按重量百分比它们分别占如下比例：水泥40-60、硅酸钙1-55、精沙15-79、石棉15-25,所述底料层由水泥、陶粒和沙子制成，按重量百分比计，水泥17-25，陶粒和沙子75-83。本专利技术在底料层中以硅酸钙、陶粒作主要成份，由于陶粒具有散热系数低的特性，所以大大的提高了砖的保温性能，在砖的面料层使用彩色水泥，它代替了现在在建筑物外表面贴彩釉砖的麻烦，减少了开支，节约了成本，而且消除了彩釉瓷砖日后剥蚀脱落的不安全因素。在砖的面料层使用硅酸钙，强度高，保温性强。所以使用硅酸钙制成的保温砖具有外隔热内保温、外装饰与砌筑墙体一次完成，有效节约能源，有利于降低建筑成本之功能。具体实施方式：下面结合实施例对本专利技术做进一步说明：建筑外墙装饰材料，它包括面料层和底料层，面料层由水泥、硅酸钙、石棉和精沙制成，按重量百分比它们分别占如下比例：彩色水泥40-60、硅酸钙...
【技术保护点】
一种建筑外墙装饰材料，它包括面料层和底料层构成，其特征在于：所述面料层由彩色水泥、硅酸钙、石棉和精沙制成，按重量百分比例：彩色水泥40‑60 、硅酸钙1‑55、精沙 15‑79、石棉15‑25 , 所述底料层由水泥、陶粒和沙子制成，按重量百分比：水泥17‑25 、陶粒和沙子75‑83 。
【技术特征摘要】
1.一种建筑外墙装饰材料，它包括面料层和底料层构成，其特征在于：所述面料层由彩色水泥、硅酸钙、石棉和精沙制成，按重量百分比例：彩色水泥40-60...