Undismantled mould of the invention discloses a fire retardant and its preparation process is as follows: 1 in the automatic plate forming machine on the bottom of the first layer of glass fiber cloth; 2 filling slurry; 3 surface with a layer of glass fiber cloth; 4 curing, demoulding, trimming and. According to the mass ratio of the slurry, seven water solution of 24 Baume Magnesium Sulfate 30 degrees 50, light burned magnesia powder 25 35 copies, 30 copies and 10 wood powder 0.005 0.015 additive mixing at room temperature. The invention relates to a template free fire, with no formaldehyde, halogenation, moisture protection, high strength, long service life, a fire, low cost, safety and environmental protection as a building template material has broad application prospect.
【技术实现步骤摘要】
一种防火的免拆模板
本专利技术属于建筑模板材料领域的
，具体是一种防火的免拆模板。
技术介绍
住宅作为衡量一个国家经济和人民生活水平的一项重要指标，其建筑材料的安全性，耐久性，保温性，易施工性等是提高住宅质量、改善居住环境的重要手段。轻质、高强的镁质材料在当代的建筑中，越来越受到广泛的应用。目前市场上广泛使用木模板或金属模板，它们可以回收反复使用，一定程度上节约了资源，但施工环境的多样性，存在一些不易拆除模板的施工环境，例如隧道、筏式基础、下水道、地下铁、挡土墙、储槽、高层建筑、海洋工程等，需要采用免拆模板更为合理，为施工带来便捷。
技术实现思路
本专利技术提供了以下技术方案:一种防火的免拆模板，其制备工艺为：1在自动板材成型机上底层先铺一层玻纤网格布；2填充浆料；3表层再加一层玻纤网格布；4固化成型，脱模，切边而成。其浆料按照质量比为，波美度为24-30°的七水硫酸镁溶液50份，轻烧氧化镁粉25-35份，木粉10-30份以及0.005-0.015份添加剂常温混合均匀。优选地，所述添加剂按照质量配比为木质素磺酸钠3-5份，七水硫酸铝钾40-60份，磷酸二氢钠100-120份以及水2000-2500份组成。优选地，所述木粉的颗粒大小为0.1-3mm。优选地，所述免拆模板中至少有两层玻纤网格布。本专利技术的优点在于采用硫酸镁代替氯化镁，从源头杜绝了板材中氯离子的摄入，是原有板材吸潮、开裂、变形、腐蚀螺钉的现象得到改善，使镁质板材性能更稳定、产品使用寿命更长；应用木粉代替其他无机添加材料，将可再生资源合理利用，变废为宝，节能又环保，同时提高了板材的保温性能；免...
【技术保护点】
一种防火的免拆模板，其制备工艺为：1在自动板材成型机上底层先铺一层玻纤网格布；2填充浆料；3表层再加一层玻纤网格布；4固化成型，脱模，切边而成，其浆料按照质量比为，波美度为24‑30°的七水硫酸镁溶液50份，轻烧氧化镁粉25‑35份，木粉10‑30份以及0.005‑0.015份添加剂常温混合均匀。
【技术特征摘要】
1.一种防火的免拆模板，其制备工艺为：1在自动板材成型机上底层先铺一层玻纤网格布；2填充浆料；3表层再加一层玻纤网格布；4固化成型，脱模，切边而成，其浆料按照质量比为，波美度为24-30°的七水硫酸镁溶液50份，轻烧氧化镁粉25-35份，木粉10-30份以及0.005-0.015份添加剂常温混合均匀。2.根据权利要求1所述的添...
【专利技术属性】
技术研发人员：白红太，李兴华，
申请(专利权)人：山西金辰绿环建筑技术有限公司，
类型：发明
国别省市：山西,14