The invention discloses a high strength weathering type refractory brick, it consists of the following parts by weight of raw materials: coal gangue 60 70 copies, 25 copies of 15 coal, 10 20 basalt. The preparation method is as follows: (1) the coal gangue to the particle size of 0.3 0.6mm, basalt crushed to particle size 0.1 0.4mm; (2) the step (1) obtained the coal gangue powder, basalt powder and slime mixing, stirring, adjustment of water content to 13 (3) will be 16%. Step (2) after the treatment of raw materials are pressed into bricks, the ageing 24 48 hours; (4) will be sent to the Chen Huahao brick baking furnace roasting; roasting method is: first in the 130 140 C 7 preheat for 9 minutes, then quickly heating up to 1000 1050 C 18 roasting for 24 hours. Mainly used in refractory brick field.
【技术实现步骤摘要】
一种新型耐火砖及其制备方法
本专利技术属于耐火砖领域,具体涉及一种高强度耐候型耐火砖。
技术介绍
煤矸石是在成煤过程中与煤共同沉积的有机化合物和无机化合物混合在一起的岩石,通常呈薄层和在煤层中或煤层顶、煤层底。煤矸石按主要矿物含量分为黏土岩类、砂石岩类、碳酸盐类、铝质岩类。按来源及最终状态,煤矸石可分为掘进矸石、选煤矸石和自然矸石三大类。煤矸石排放量根据煤层条件、开采条件和洗选工艺的不同有较大差异,一般掘进矸石占原煤产量的10%左右,选煤矸石占入选原煤量的12%~18%。煤矸石的无机成分主要是硅、铝、钙、镁、铁的氧化物和某些稀有金属。其化学成分组成的百分率:SiO2为52~65;Al2O3为16~36;Fe2O3为2.28~14.63;CaO为0.42~2.32;MgO为0.44~2.41;TiO2为0.90~4;P2O5为0.007~0.24;K2O+Na2O为1.45~3.9;V2O5为0.008~0.03。煤矸石弃置不用,占用大片土地。煤矸石中的硫化物逸出或浸出会污染大气、农田和水体。矸石山还会自燃发生火灾,或在雨季崩塌,淤塞河流造成灾害。中国积存煤矸石达10亿吨以上,每年还将排出煤矸石1亿吨。煤泥泛指煤粉含水形成的半固体物,是煤炭生产过程中的一种产品,根据品种的不同和形成机理的不同,其性质差别非常大,可利用性也有较大差别,其种类众多,用途广泛。由于煤泥具有高水分、高粘性、高持水性和低热值等诸多不利条件,很难实现工业应用,长期被电力用户拒之门外,以民用地销为主要出路。改革开放以来,国民经济有了迅猛的发展,煤炭产量已跃居世界首位,市场形势也发生了很大变 ...
【技术保护点】
一种高强度耐候型耐火砖,其特征在于,它由以下重量份的原料组成:煤矸石 60‑70份,煤泥 15‑25份,玄武岩 10‑20份。
【技术特征摘要】
1.一种高强度耐候型耐火砖,其特征在于,它由以下重量份的原料组成:煤矸石60-70份,煤泥15-25份,玄武岩10-20份。2.根据权利要求1所述的一种高强度耐候型耐火砖,它由以下重量份的原料组成:煤矸石65份,煤泥20份,玄武岩15份。3.根据权利要求1或2所述的一种高强度耐候型耐火砖的制备方法,其特征在于,包括如下步骤:(1)将煤矸石破碎至粒径0.3-0.6mm,将玄武岩破碎至粒径0.1-0.4mm;(2)将步骤(1)得到的煤矸石粉末、玄武岩粉末与煤泥混合,搅拌均匀,调整含水率至13-16%,(3)将步骤(2)处理后的原料压制成砖坯,放置陈化24-...
【专利技术属性】
技术研发人员:蒙永平,赵正俊,王勇,
申请(专利权)人:四川乔丰新材料科技有限公司,
类型:发明
国别省市:四川,51