The invention discloses a jet spinning blended fabric, which comprises the following steps: feeding synthetic fiber after drafting, once Laura output shall meet the design fineness, then causes the strips to be after the first and second nozzle of air nozzle in twisting and rotating at a speed of 300000r/min, to be a first airflow nozzle by first complete condensation and straight, then the second nozzle part of fiber surface, and in a certain twist angle and surface pressure bag wrapped in another part of the core fiber, so continuous, the 250m/min~300m/min line speed wound into the package, the final product form. By the way, the fabric is soft and delicate, smooth, moisture wicking, antibacterial.
【技术实现步骤摘要】
本专利技术涉及一种混纺织物的喷气纺纱工艺。
技术介绍
随着人们生活水平的提高,对穿着的时尚度要求也越来越高,尤其是对纺织原料的二次利用越来越有兴趣。再生棉雪花混纺纱是一种国际国内流行的绿色时尚环保纱线,由于用此纱线生产的面料的外观呈现雪花状效果,所以又称为“雪花混纺纱”。但雪花混纺纱在纺纱过程中,配棉用料难以混合均匀,从而导致了雪花混纺纱的成纱强力低、棉结高的问题。因此,设计一种能够提高成纱强力并降低棉结的再生棉雪花混纺纱及其混纺工艺是至关重要的。
技术实现思路
本专利技术主要解决的技术问题是:提供一种混纺织物的喷气纺纱工艺,得到的面料柔软细腻,滑爽、吸湿排汗、抗菌卫生。为解决上述技术问题,本专利技术采用的一个技术方案是:提供一种混纺织物的喷气纺纱工艺,包括以下步骤:喂入合成纤维经过罗拉牵伸后,从前罗拉输出的须条达到设计的细度,然后使须条经过第一、第二喷嘴进行加捻,喷嘴中的气流以300000r/min的速度进行回转,须条首先经第一喷嘴的气流作用完成凝聚与伸直,然后被第二喷嘴分离出一部分表层纤维,并以一定的捻角和压力包缠在另一部分中芯纤维的表面,如此连续进行,最后以250m/min~300m/min的线速度卷绕成筒子,所形成的最终产品。在本专利技术一个较佳实施例中,所述合成纤维是涤纶、锦纶混纺而成。在本专利技术一个较佳实施例中,所述涤纶和锦纶的比例为2:1。本专利技术的有益效果是:得到的面料柔软细腻,滑爽、吸湿排汗、抗菌卫生。具体实施方式下面结合对本专利技术的较佳实施例进行详细阐述,以使本专利技术的优点和特征能更易于被本领域技术人员理解,从而对本专利技术的保护 ...
【技术保护点】
一种混纺织物的喷气纺纱工艺,其特征在于:包括以下步骤:喂入合成纤维经过罗拉牵伸后,从前罗拉输出的须条达到设计的细度,然后使须条经过第一、第二喷嘴进行加捻,喷嘴中的气流以300000r/min的速度进行回转,须条首先经第一喷嘴的气流作用完成凝聚与伸直,然后被第二喷嘴分离出一部分表层纤维,并以一定的捻角和压力包缠在另一部分中芯纤维的表面,如此连续进行,最后以250m/min~300m/min的线速度卷绕成筒子,所形成的最终产品。
【技术特征摘要】
1.一种混纺织物的喷气纺纱工艺,其特征在于:包括以下步骤:喂入合成纤维经过罗拉牵伸后,从前罗拉输出的须条达到设计的细度,然后使须条经过第一、第二喷嘴进行加捻,喷嘴中的气流以300000r/min的速度进行回转,须条首先经第一喷嘴的气流作用完成凝聚与伸直,然后被第二喷嘴分离出一部分表层纤维,并以一定的捻角和压...
【专利技术属性】
技术研发人员:沈旭初,
申请(专利权)人:太仓市梓怡纺织有限公司,
类型:发明
国别省市:江苏;32