The invention provides a PVA, collagen and feather fiber composite fiber materials, the preparation method comprises the following steps: 1) were equipped with PVA solution, the solution of collagen and feather fiber solution; 2) step 1) solution compound, crosslinking agent and defoaming agent, made by wet spinning solution; 3) spinning technology, prepared by PVA, collagen and feather fiber composite fiber spun fiber; 4) PVA, collagen and feather fiber composite fiber spun fibers after heat drawing and heat setting and acetalization, PVA, collagen and feather fiber composite fiber products. The invention of PVA, collagen and feather fiber composite fiber material is a kind of high strength and good spinnability of fiber materials.
【技术实现步骤摘要】
一种PVA、胶原蛋白和鸭绒纤维复合化纤材料
本专利技术涉及一种PVA、胶原蛋白和鸭绒纤维复合化纤材料，属于化工材料
技术介绍
胶原蛋白纤维是一种动物蛋白质改性的合成纤维，其原料为动物蛋白及羟基、氰基高聚物，是一种可降解的环保纤维。胶原蛋白纤维具有蚕丝般的光泽、羊绒般的轻柔糯滑、麻纤维的吸湿快干等特点，能够满足人们对服饰自然化、舒适化、休闲化、个性化的追求。胶原蛋白纤维的不足之处是吸水性强，可纺性差。因此，需要与可纺性好的纤维组成复合化纤，才能有效应用。
技术实现思路
本专利技术的目的是克服现有技术的不足之处，提供一种PVA、胶原蛋白和鸭绒纤维复合化纤材料。本专利技术的PVA、胶原蛋白和鸭绒纤维复合化纤材料，其制备方法包括如下步骤：1）分别配置PVA溶液、胶原蛋白溶液和鸭绒纤维溶液；2）将步骤1）的溶液复合，添加交联剂和消泡剂，制成纺丝原液；3）采用湿法纺丝技术，制备得到PVA、胶原蛋白和鸭绒纤维复合化纤初生纤维；4）将PVA、胶原蛋白和鸭绒纤维复合化纤初生纤维,经过热拉伸、热定型和缩醛化处理，得到PVA、胶原蛋白和鸭绒纤维复合化纤成品。优选地，所述的步骤2）中，PVA、胶原蛋白和鸭绒纤维的摩尔比为（1-2）：1：1；所述的步骤2）中，交联剂为戊二醛交联剂。所述的步骤3）中，湿法纺丝温度为60-70℃。本专利技术的PVA、胶原蛋白和鸭绒纤维复合化纤材料是一种可纺性高、强度好的化纤材料。具体实施方式实施例1本专利技术的PVA、胶原蛋白和鸭绒纤维复合化纤材料，其制备方法包括如下步骤：1）分别配置PVA溶液、胶原蛋白溶液和鸭绒纤维溶液；2）将步骤1）的溶液复...
【技术保护点】
一种PVA、胶原蛋白和鸭绒纤维复合化纤材料，其特征在于，其制备方法包括如下步骤：1）分别配置PVA溶液、胶原蛋白溶液和鸭绒纤维溶液；2）将步骤1）的溶液复合，添加交联剂和消泡剂，制成纺丝原液；3）采用湿法纺丝技术，制备得到PVA、胶原蛋白和鸭绒纤维复合化纤初生纤维；4）将PVA、胶原蛋白和鸭绒纤维复合化纤初生纤维,经过热拉伸、热定型和缩醛化处理，得到PVA、胶原蛋白和鸭绒纤维复合化纤成品。
【技术特征摘要】
1.一种PVA、胶原蛋白和鸭绒纤维复合化纤材料，其特征在于，其制备方法包括如下步骤：1）分别配置PVA溶液、胶原蛋白溶液和鸭绒纤维溶液；2）将步骤1）的溶液复合，添加交联剂和消泡剂，制成纺丝原液；3）采用湿法纺丝技术，制备得到PVA、胶原蛋白和鸭绒纤维复合化纤初生纤维；4）将PVA、胶原蛋白和鸭绒纤维复合化纤初生纤维,经过热拉伸、热定型和缩醛化处理，得到PVA、胶原蛋白和鸭绒纤维复合化纤成...
【专利技术属性】
技术研发人员：杨忠国，
申请(专利权)人：海安县中山合成纤维有限公司，
类型：发明
国别省市：江苏,32