The name of the invention is light agitation produced by catalytic pressure chloride modified chlorinated paraffin method, which belongs to the technical field of chlorinated paraffin, chlorinated paraffin production in order to improve the speed of the original 87106851.6 patent technology improved the solution is Shi Lazhong catalyst increased ketone peroxide based on reactor pressure is increased to 1 kg / cm2, kettle is provided with the light source the paraffin, raw material is heated to a certain temperature (110 degrees Celsius), and then according to a certain proportion (about 5%) with polyethylene melting, and then put the kettle to heat and ensure the chloride, polyethylene as the melting state, provides a method for producing a more rapid.
【技术实现步骤摘要】
催化加压光氯化鼓动法生产改性氯化石蜡方法(一)
：本专利技术涉及一种生产改性氯化石蜡的方法。(二)
技术介绍
：“强制循环鼓动法生产氯化石蜡装置”(原专利号：87106851.6)其技术方案是：将氯气送入反应釜空间，氯气和反应生成的氯化氢气体抽出，经喷射泵和贮液槽，被水吸收，余下氯气鼓压进鼓动器，如此连续快速反应。但用于生产氯化石蜡速度还不够理想，尤其是生产高氯化石蜡产品，到反应后期，速度趋缓。(三)
技术实现思路
：本专利技术的任务是基于对原87106851.6专利技术专利的一种改进，提供一种更快的生产改性氯化石蜡的方法，采取的技术方案是加催化剂，装置提高压力，釜内加装上光源，把原料石蜡加热到一定温度(110℃左右)，然后按一定比例(5％左右)加入聚乙烯进行加热熔化，然后投入釜内氯化，并以热确保聚乙烯为熔化状。这样在强制循环鼓动下提高反应速度。(四)具体实施方式：一套“强制循环鼓动法生产氯化石蜡装置”，使用500升反应釜，预先在石蜡中加入酮类过氧化物，浓度为0.01～6.00％，使装置内压力提高到1公斤/平方厘米，其反应釜内加装1000瓦汞灯。把原料石蜡加热到一定温度(110℃左右)，然后按一定比例(5％左右)加入聚乙烯进行加热熔化，然后投入釜内氯化，并以热确保聚乙烯为熔化状。本专利技术操作与“强制循环鼓动法生产氯化石蜡装置”同。
【技术保护点】
一种催化加压光氯化鼓动法生产改性氯化石蜡方法，包括把氯气和氯化氢气体抽出，氯化氢气体在喷射泵和贮液槽被水吸收，余下氯气鼓压进鼓动器，如此连续，其特征是：石蜡中加入浓度为0.01～6.00％酮类过氧化物催化，增加反应压力，釜内装有光源氯化，把原料石蜡加热到一定温度(110℃左右)，然后按一定比例(5％左右)加入聚乙烯进行加温熔化，然后投入釜内氯化，并以热确保聚乙烯为熔化状。
【技术特征摘要】
1.一种催化加压光氯化鼓动法生产改性氯化石蜡方法，包括把氯气和氯化氢气体抽出，氯化氢气体在喷射泵和贮液槽被水吸收，余下氯气鼓压进鼓动器，如此连续，其特征是：石蜡中加入浓度为0.01～6.0...