The invention discloses a polymer cable material with high temperature resistance, which comprises the following components: the weight of a glass fiber 30 70 copies, 5 copies of the 20 polyimide fiber, 10 polypropylene 60, hydrogenated nitrile rubber 12 35, four 2 15 pentaerythritol hydrosulfuryl acetate, A 151 silane coupling agent 3 12 copies, 4 copies of the 12 magnesium hydroxide whisker, barium sulfate 2 10, thio two propionic acid laurate two 2 8 and 1010 5 15 copies of antioxidant. The invention adopts the high temperature resistance, corrosion resistance, good insulation properties of the glass fiber made of polymer materials, using 1010 antioxidants, can delay aging of polypropylene, can make the anti ageing properties of polymer materials.
【技术实现步骤摘要】
一种耐高温的高分子电缆材料
本专利技术属于高分子材料
，具体涉及一种耐高温的高分子电缆材料。
技术介绍
常用的电线、电缆按用途可分为裸导线、绝缘电线、耐热电线、屏蔽电线、电力电缆、控制电缆、通信电缆、射频电缆等。电力系统采用的电线电缆产品主要有架空裸电线、汇流排（母线）、电力电缆（塑料线缆、油纸力缆（基本被塑料电力电缆代替）、橡套线缆、架空绝缘电缆）、分支电缆（取代部分母线）、电磁线以及电力设备用电气装备电线电缆等。用于电力电缆的绝缘层材料需要具备以下性能：（1）高的击穿强度；（2）低的介质损耗；（3）相当高的绝缘电阻；（4）优良的耐放电性能；（5）具有一定的柔软性和机械强度；（6）绝缘性能长期稳定。高分子材料在电缆材料中有着较广的用途，由于上述性质的要求，用于电缆材料的高分子材料也需要具备较高的机械强度如弯曲强度、拉伸强度等。同时，作为电缆材料使用时，需要耐温高、抗腐、绝缘性能好、抗老化等功能。
技术实现思路
本专利技术的目的在于针对现有技术的不足，现提供一种耐高温的高分子电缆材料。为解决上述技术问题，本专利技术采用的技术方案为：一种耐高温的高分子电缆材料，其创新点在于：包括以下重量份的成分：玻璃纤维30-70份、聚酰亚胺纤维5-20份、聚丙烯10-60份、氢化丁腈橡胶12-35份、季戊四醇四巯基乙酸酯2-15份、A-151硅烷偶联剂3-12份、氢氧化镁晶须4-12份、硫酸钡2-10份、硫代二丙酸二月桂酸酯2-8份、1010抗氧剂5-15份。进一步的，一种耐高温的高分子电缆材料，包括以下重量份的成分：玻璃纤维40-60份、聚酰亚胺纤维10-15份、聚丙...
【技术保护点】
一种耐高温的高分子电缆材料，其特征在于：包括以下重量份的成分：玻璃纤维30‑70 份、聚酰亚胺纤维5‑20 份、聚丙烯10‑60 份、氢化丁腈橡胶12‑35 份、季戊四醇四巯基乙酸酯2‑15 份、A‑151硅烷偶联剂 3‑12 份、氢氧化镁晶须4‑12 份、硫酸钡2‑10 份、硫代二丙酸二月桂酸酯2‑8 份、1010抗氧剂 5‑15 份。
【技术特征摘要】
1.一种耐高温的高分子电缆材料，其特征在于：包括以下重量份的成分：玻璃纤维30-70份、聚酰亚胺纤维5-20份、聚丙烯10-60份、氢化丁腈橡胶12-35份、季戊四醇四巯基乙酸酯2-15份、A-151硅烷偶联剂3-12份、氢氧化镁晶须4-12份、硫酸钡2-10份、硫代二丙酸二月桂酸酯2-8份、1010抗氧剂5-15份。2.根据权利要求1所述的一种耐高温的高分子电缆材料，其特征在于：包括以下重量份的成分：玻璃纤维40-60份、聚酰亚胺纤维10-15份、聚丙烯30-40份...
【专利技术属性】
技术研发人员：潘征鹏，
申请(专利权)人：南通久聚高分子科技有限公司，
类型：发明
国别省市：江苏,32