The invention relates to a silane crosslinked polyethylene material field, in particular to a method for preparing silane crosslinked mixture and rapid crosslinking at room temperature, LLDPE, DCP, silane 151, antioxidant 1010, processing aid in vacuum drum dryer in 50 60 degrees rotation stirring and vacuum stirring for 2 hours; then adding hydrated alumina, glycerol after 1 hours of stirring. The preparation method of silane crosslinked crosslinking mixture quickly provided at room temperature, in the production process of silane crosslinked material, adding water compounds and water absorbent materials of the cable by means of water of crystallization water in the crystal in the coordination of water absorbent crosslinked to form in a relatively short period of time, often at room temperature wet conditions, improve production efficiency.
【技术实现步骤摘要】
常温下快速交联的硅烷交联混合物及其制备方法
本专利技术涉及一种硅烷交联聚乙烯材料领域，具体为常温下快速交联的硅烷交联混合物及其制备方法。
技术介绍
硅烷交联聚乙烯具有良好的电性能、抗老化性，并且物理机械性能优异广泛应用于电线电缆行业，但都存在必须在温水中烧煮或蒸汽房中蒸煮很长时间。严重影响了交联电缆的生产效率。
技术实现思路
针对上述技术问题，本专利技术提供一种可以在常温下快速交联的硅烷交联混合物及其制备方法。具体的技术方案为：常温下快速交联的硅烷交联混合物，由以下原料按照重量份数组成：LLDPE（线性低密度聚乙烯）100DCP0.1-0.15硅烷1510.8-1.0抗氧剂10100.3-0.4加工助剂0.2-0.4水合三氧化铝4-5丙三醇0.5-1.0。常温下快速交联的硅烷交联混合物的制备方法，包括以下过程：（1）将LLDPE（线性低密度聚乙烯）、DCP、硅烷151、抗氧剂1010、加工助剂在抽真空转鼓干燥器在50-60℃转动搅拌并抽真空搅拌2小时；（2）再加入水合氧化铝、丙三醇后继续搅拌1小时。该硅烷交联混合物用于电缆制备，挤塑成缆后，在常温常湿情况下4小时后，材料交联率达到65%。本专利技术提供的常温下快速交联的硅烷交联混合物的制备方法，在生产硅烷交联料的过程中，加入含水化合物和吸水剂，使材料成缆后借助含水结晶物中的结晶水在吸水剂的协调下在常温、常湿的条件下在较短的时间里形成交联，提高了生产效率。具体实施方式结合实施例说明本专利技术的具体实施方式。实施例1以下原料按照重量份数量取：LLDPE100DCP0.15硅烷1510.9抗氧剂10100.4加工助剂...
【技术保护点】
常温下快速交联的硅烷交联混合物，其特征在于，由以下原料按照重量份数组成：LLDPE（线性低密度聚乙烯） 100DCP 0.1‑0.15硅烷 151 0.8‑1.0抗氧剂 1010 0.3‑0.4加工助剂 0.2‑0.4水合三氧化铝 4‑5丙三醇 0.5‑1.0。
【技术特征摘要】
1.常温下快速交联的硅烷交联混合物，其特征在于，由以下原料按照重量份数组成：LLDPE（线性低密度聚乙烯）100DCP0.1-0.15硅烷1510.8-1.0抗氧剂10100.3-0.4加工助剂0.2-0.4水合三氧化铝4-5丙三醇0.5-1.0。2.根据...
【专利技术属性】
技术研发人员：张立阳，狄惠新，杨凯，吴林磊，薛仁君，石海，
申请(专利权)人：江苏宝安电缆有限公司，
类型：发明
国别省市：江苏,32