The invention discloses a PVC fireproof plate, the invention is made of polyvinyl chloride resin and dioctyl phthalate two formic acid two, three base lead sulfate, barium stearate, talcum powder, calcium carbonate, flame retardant, coupling agent prepared by mixing. PVC fire proof plate of the invention, mainly PVC resin as the main material, and the amount of talcum powder, calcium carbonate and other medium, improves the sheet resistance ability, and use a variety of compound flame retardants, the plate has good flame retardant and smoke, obvious effect, high temperature heat. The board is light in material, excellent in fire protection, waterproof, anti-corrosion and low in price. It conforms to the national green building materials industry policy and can be used for ceiling, partition walls, pipes and so on.
【技术实现步骤摘要】
一种PVC防火板材
本专利技术涉及建筑材料领域，具体涉及一种防火板材。
技术介绍
防火板材的用途非常多，可以用于建筑物外墙、内墙、临时房屋等的建设当中。防火性能对板材的性能影响较大，若板材防火性能较差，则会有较大的安全隐患。若遇到明火，导致板材迅速燃烧，则会造成严重的财产损失。此外，如果板材的耐高温效果较差，在高温情况下，板材长时间受热后，会产生一定的形变，对建筑物的稳定性产生极大的考验，因此我们需要寻找一种具有良好防火和耐高温性能的板材。
技术实现思路
本专利技术目的在于，提供一种PVC防火板材，本专利技术采用的技术方案如下：一种PVC防火板材，其特征在于，由以下组分按重量百分比混合制备而成：聚氯乙烯树脂35-65份邻苯二甲酸二辛脂5-20份三盐基硫酸铅5-10份硬脂酸钡1-5份滑石粉5-20份碳酸钙10-20份防燃剂1-10份偶联剂1-5份。优选地，所述的防燃剂包括有机二茂铁，硼酸锌，三氧化钼，氢氧化铝，玻璃微珠，粉煤灰。优选地，所述的防燃剂是由有机二茂铁，硼酸锌，三氧化钼，氢氧化铝，玻璃微珠，粉煤灰按照重量百分比为1：2：1：2：1：2混合组成。优选地，所述的偶联剂包括有机硅烷，马来酸酐接枝聚烯烃。本专利技术相对于现有技术的有益效果是：本专利技术的PVC防火板材，主要以聚氯乙烯树脂为主要材料，并适量的滑石粉，碳酸钙等介质，提高了板材的抗压能力，同时复配使用多种防燃剂，使得板材具有良好的阻燃作用，而且消烟效果明显，遇热时能耐高温。该板材质轻，具有优良的防火，防水性能，防腐蚀，价格低廉，符合国家绿色环保建材产业政策，可用于吊顶，隔墙，管道等。具体实施方式以下...
【技术保护点】
一种PVC防火板材，其特征在于，由以下组分按重量百分比混合制备而成：聚氯乙烯树脂 35‑65份邻苯二甲酸二辛脂 5‑20份三盐基硫酸铅 5‑10份硬脂酸钡 1‑5份滑石粉 5‑20份碳酸钙 10‑20份防燃剂 1‑10份偶联剂 1‑5份。
【技术特征摘要】
1.一种PVC防火板材，其特征在于，由以下组分按重量百分比混合制备而成：聚氯乙烯树脂35-65份邻苯二甲酸二辛脂5-20份三盐基硫酸铅5-10份硬脂酸钡1-5份滑石粉5-20份碳酸钙10-20份防燃剂1-10份偶联剂1-5份。2.根据权利要求1所述的PVC防火板材，其特征在于，所述的防燃剂包括有机二茂铁，硼酸...